Continuous refill crystal growth method
AssigneeHoriba Instruments, Inc.
InventorKiril A. Pandelisev
Life of this patent
Estimating the term…
Abstract
Large crystals of alkali halide materials are presently produced using the Bridgman-Stockbarger method and result in state-of-the-art crystals of up to 30" in diameter and 20" in height. Both residual impurity concentrations and dopant concentrations have been difficult to control because the segregation coefficients are not equal to unity. As a result, the residual impurity and dopant concentrations can vary drastically across the length of the crystal. By adding additional charging material to the melt during the crystallization process, the residual impurity and dopant concentrations can be kept nearly constant throughout the length of the crystal. By adding charging material to the melt during crystallization, the overall length of a manufactured crystal can be increased dramatically.
Claims8
A method of growing essentially single crystals of substantially uniform composition comprising the steps of:
- forming a melt of an alkali halide salt in a crucible;
- progressively cooling the metal to crystalize the alkali halide salt in said crucible in a Bridgman-Stockbarger type furnace apparatus;
- and
- adding additional liquefied charging material to the melt in the crucible after crystallization has begun;
- wherein the alkali halide salt includes a dopant and wherein the crystallization step normally increases the concentration of the dopant in the melt as compared with the crystallized alkali halide salt;
- and
- wherein the step of adding additional material involves adding alkali halide salt having less dopant than is present in said melt;
- whereby the dopant concentration in the crystallized alkali halide salt is maintained substantially constant.
A method of growing essentially single crystals of substantially uniform composition comprising the steps of:
- forming a melt of an alkali halide salt in a crucible;
- progressively cooling the melt to crystalline the alkali halide salt in said crucible in a bridgman-Stockbarger type furnace apparatus;
- and
- adding additional liquefied charging material to the metal in the crucible after crystallization has begun;
- wherein the alkali halide salt includes impurities and wherein the crystallization step normally increases the concentration of the dopant in the metal as compared with the crystallized alkali halide salt;
- wherein the step of adding additional material involves adding alkali halide salt having less impurity concentration than is present in said melt;
- and
- whereby the impurity concentration in the crystallized alkali halide salt is maintained substantially constant.
A method of growing essentially single crystals of substantially uniform composition comprising the steps of:
- forming a melt of an alkali halide salt in a crucible;
- progressively cooling the melt to crystalize the alkali halide salt in said crucible in a Bridgman-Stockbarger type furnace apparatus;
- and
- adding additional liquefied charging material to the melt in the crucible after crystallization has begun;
- wherein the alkali halide salt includes a dopant;
- and
- wherein the step of adding additional material involves adding alkali halide salt having different dopant concentration than is present in said melt.
A method of growing essentially single crystals of substantially uniform composition comprising the steps of:
- forming a melt of an alkali halide salt in a crucible;
- progressively cooling the metal to crystalize the alkali halide salt in said crucible in a Bridgman-Stockbarger type furnace apparatus;
- and
- adding additional liquefied charging material to the metal in the crucible after crystallization has begun;
- wherein the alkali halide salt includes a dopant;
- wherein the step of adding additional material involves adding alkali halide salt having different dopant concentration than is present in said melt;
- and
- whereby the dopant concentration in the crystallized alkali halide salt remains essentially constant from the beginning of the crystal to the end.
Dependencies are inferred from the claim text.