Aqueous based, strippable coating composition and method
AssigneeGroco Specialty Coatings Company
InventorsGeorge W. Grogan, Robert H. Boyd
Life of this patent
Estimating the term…
Abstract
A strippable coating composition is shown for use as a temporary protective coating on a variety of substrates. The composition includes a water based polymeric emulsion which is dispersed in an aqueous carrier to form a stable emulsion. Release aids are incorporated in the composition which allow the protective coating to be removed by peeling or washing off with water.
Claims2
A clear, strippable coating composition applied as a film which when dried has a thickness in the range from about 1.5 to 5.0 mils, the strippable coating composition, comprising:
- a blend of non-volatile components comprising about 41-71% by weight of the coating composition, including:
- about 34-54% by weight polyvinyl acetate emulsion;
- about 7-15% by weight of a release agent selected from the group consisting of paraffin wax emulsion, polyvinyl alcohol and mixtures thereof;
- about 0.1-0.6% by weight non-ionic surfactant as a wetting aid;
- about 0.1-0.6% by weight defoamer;
- about 0.1-0.8% by weight dispersing aid;
- and
- about 1-5% by weight thickener;
- the strippable coating composition also comprising about 29-59% by weight of the coating composition of volatile components, including:
- about 0.1-2.5% by weight plasticizer the plasticizer component being selected from the group consisting of glycerine, dibutylphthalate and 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;
- about 28.9-56.5% by weight water;
- the strippable coating composition being characterized as drying to form a clear film which is strippable for up to one year by water spray.
A clear, strippable coating composition adapted to form a temporary protective coating for a vehicle exterior surface when applied as a film which, when dried, has a thickness in the range from about 1.5 to 5.0 mils, the strippable coating composition, comprising:
- a blend of non-volatile components comprising about 41-71% by weight of the coating composition, including:
- about 34-54% by weight polyvinyl acetate emulsion;
- about 7-15% by weight of a release agent which comprises a mixture of paraffin wax emulsion and polyvinyl alcohol, the weight ratio of polyvinyl alcohol to paraffin wax emulsion in the mixture being in the range from about 1:1 to about 2:1;
- about 0.1-0.65 by weight non-ionic surfactant as a wetting aid, the non-ionic surfactant being a nonylphenol polyethylene glycol ether;
- about 0.1-4 0.6% by weight defoamer;
- about 0.1-0.8% by weight phosphate ester dispersing aid sold commercially as STRODEX PK-90, having a boiling point of 212.degree. F. and a specific gravity of 1.15;
- and
- about 1-5% by weight hydroxyethylcellulose as a thickener;
- the strippable coating composition also comprising about 29-59% by weight of the coating composition of volatile components, including:
- about 0.1-2.5% by weight plasticizer, the plasticizer component being selected from the group consisting of glycerine, dibutyl phthalate, and 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;
- and
- about 28.9-56.5% by weight water;
- the strippable coating composition being characterized as drying to form a clear film which is strippable for up to one year by water spray.
Dependencies are inferred from the claim text.