Elastomeric structures having controlled surface release characteristics
AssigneeThe Firestone Tire & Rubber Company
InventorsCleo M. Williams, Myron D. Sanders, William C. Cook
Life of this patent
Estimating the term…
Abstract
Elastomer structures having exposed controlled surface release characteristics can be made by coating at least a portion of their surface with a releasing composition comprising (a) a chlorosulphonated polymer; (b) a reinforcing filler and (c) a green tackifying agent. Optionally, these compositions can also contain a chemical curing system and one or more volatile solvent/diluent viscosity-reducing vehicle. In a specific example, the coating are applied to flexible structures used in machines for the manufacture of articles having natural tack due to their rubber or elastomer content.
Claims3
A bladder, for use in a tire assembly machine having about 10-90% of its outer surface bearing an exposed releasing surface coating of release-effective thickness formed by the method comprising the steps of:
- (I) Applying to the outer surface of the bladder a releasing composition comprising:
- (a) a chlorosulphonated polyethylene having a Mooney viscosity of about 30-160;
- (b) a carbon black or silica reinforcing filler;
- (c) a green tackifying agent;
- and optionally
- (d) a suitable chemical curing system;
- and optionally
- (e) a first inert, volatile solvent/diluent viscosity-reducing vehicle for components (a)-(d), and optionally
- (f) a second, inert volatile solvent/diluent viscosity-reducing vehicle;
- (II) Removing a sufficient amount of vehicles present to leave a coherent, adhering film on the surface;
- and
- (III) Curing the film to form the exposed releasing coating consisting essentially of said chlorosulphonted polyethylene (a), said carbon black or silica filler (b), said green tackifying agent (c) and optionally said chemical curing system (d).
A fabric reinforced turnup bladder, TUB, for use in a tire assembly machine, having at least about 10-95% of its surface covered with a fracture-resistant, exposed releasing surface of release effective thickness for an elastomeric structure formed by the method which comprises the steps of:
- (I) Applying Chemlok 234B or 234B-E in an inert solvent/diluent vehicle to at least a portion of the surface of the bladder;
- (II) Removing by evaporation at about 20.degree.-75.degree. Centigrade a sufficient amount of the vehicle present to leave a coherent, adhering film on the surface;
- and
- (III) Curing the film to form the exposed releasing coating consisting essentially of said Chemlok 234B or 234B-E;
- wherein said Chemlok 234B is a black adhesive composition containing approximately 25 weight percent of a carbon-, hydrogen-, nitrogen-, sulfur-, and chlorine-containing reside dissolved or dispersed in 50 weight percent xylene and 25 weight percent trichlorethylene, said residue exhibiting:
- (a) major absorptions in its Infrared spectrum (evaporated on a KBr plate) at 2940, 2860, 1485, 1420, 1260, 1100, 1010, 865, 780, 575 and 485 cm.sup.-1 ;
- (b) the following elemental analysis in weight percent:
- carbon, 45.49;
- hydrogen, 4.28;
- nitrogen 3.36;
- sulfur 0.5;
- and percent chlorine, 42.3;
- and (c) the following properties in weight percent:
- ash (normal) 0.59;
- methanol soluble, 43.80;
- toluene soluble, 37.45;
- said ash also containing magnesium and;
- wherein Chemlock 234B-E is the same as Chemlok 234B except it contains approximately 20-22 weight percent of said residue and monochlorotoluene trichloroethylene.
Dependencies are inferred from the claim text.