Woven textile fabric having an ultrasonically cut and sealed edge and apparatus and process for producing same

Process for ultrasonically cutting and sealing woven textile fabric to produce a clean and sharp sealed edge of a thickness no greater than the thickness of the textile fabric and having a desired wash durability without significant raveling with an ultrasonic apparatus including a vibrating sonic horn having a flat working face and an anvil positioned for contact by the vibrating horn;

• said process comprising the steps of:
• providing a wheel-shaped anvil having a beveled periphery defining therearound a peaked cutting edge, a first surface extending from the peaked cutting edge in a first direction and forming a predetermined included acute angle with the horn face of from about 3 to 20 degrees and a second surface extending from the peaked cutting edge in the opposite direction and forming an included angle with the horn face at least 21/2 degrees greater than the included angle of the first surface and no more than 45 degrees for forming a desired sharpness and for reinforcing the peaked anvil cutting edge;
• passing woven textile fabric having thermoplastic fibers through the ultrasonic apparatus and between the vibrating sonic horn and the anvil at a substantially constant predetermined rate of speed and in a generally linear path of travel substantially parallel to either the warp or the filling yarns of the fabric and with the peaked cutting edge of the anvil and positioned so that the edge of the fabric to be sealed is passed over the first surface of the anvil;
• cutting an edge through the textile fabric substantially parallel with either a warp or a filling yarn which is parallel to the path of travel of the fabric through the ultrasonic apparatus by vibrations of the sonic horn against the peaked cutting edge of the anvil;
• simultaneously sealing the cut edge of the fabric by fusing and bonding a mass of thermoplastic fibers in the fabric adjacent to and extending inwardly of the fabric from the cutting edge from about 0.01 to 0.10 inch and encompassing from about 2 to 4 of either the warp or filling yarns extending parallel to the cut edge by vibrations of the sonic horn toward the first surface of the anvil;
• and
• applying a predetermined pressure to the anvil and to the vibrating sonic horn for exerting predetermined forces on the fabric passing therebetween for aiding in the ultrasonic cutting and sealing.

Process for ultrasonically cutting and sealing woven textile fabric to produce a clean and sharp sealed edge of a thickness no greater than the thickness of the textile fabric and having a wash durability of 25 to 50 washings without significant raveling with an ultrasonic apparatus including a vibrating sonic horn having a flat working face and an anvil positioned for contact by the vibrating horn;

• said process comprising the steps of:
• providing a wheel-shaped anvil having an outside beveled periphery defining therearound a peaked cutting edge, a first surface extending from the peaked cutting edge in a first direction and forming a predetermined included angle with the horn face of from about 3 to 20 degrees and a second surface extending from the peaked cutting edge in the opposite direction and forming an included angle with the horn face at least 21/2 degrees greater than the included angle of the first surface and no more than 45 degrees for forming a desired sharpness and for reinforcing the peaked anvil cutting edge;
• passing woven textile fabric having at least 65% thermoplastic fibers through the ultrasonic apparatus and between the vibrating sonic horn and the anvil at a substantially constant predetermined rate of speed and in a generally linear path of travel substantially parallel to the warp yarns of the fabric and with the peaked cutting edge of the anvil and positioned so that the edge of the fabric to be sealed is passed over the first surface of the anvil;
• cutting an edge through the textile fabric substantially parallel with a warp yarn by vibrations of the sonic horn against the peaked cutting edge of the anvil;
• simultaneously sealing the cut edge of the fabric by fusing and bonding a mass of thermoplastic fibers in the fabric adjacent to and extending inwardly of the fabric from the cutting edge from about 0.01 to 0.10 inch and encompassing from about 2 to 4 of the warp yarns extending parallel to the cut edge by vibrations of the sonic horn toward the first surface of the anvil;
• and
• applying a predetermined pressure to the anvil and to the vibrating sonic horn for exerting predetermined forces on the fabric passing therebetween for aiding in the ultrasonic cutting and sealing.

Process for ultrasonically cutting and sealing woven textile fabric to produce a clean and sharp sealed edge of a thickness no greater than the thickness of the textile fabric and having a wash durability of 25 to 50 washings without significant raveling with an ultrasonic apparatus including a vibrating sonic horn having a flat working face and an anvil positioned for contact by the vibrating horn;

• said process comprising the steps of:
• providing a wheel-shaped anvil having an outside beveled periphery defining therearound a peaked cutting edge, a first surface extending from the peaked cutting edge in a first direction and forming a predetermined included acute angle with the horn face of from about 5 to 15 degrees and a second surface extending from the peaked cutting edge in the opposite direction and forming an included angle with the horn face at least 21/2 degrees greater than the included angle of the first surface and no more than 45 degrees for forming a desired sharpness and for reinforcing the peaked anvil cutting edge;
• passing woven textile fabric having thermoplastic and cotton fibers including about 65 to 80% thermoplastic fibers in the fabric and at least 65% thermoplastic fibers in the warp and a weight of from about 2.25 to 6.00 oz./yd.sup.2 between the vibrating sonic horn and the anvil at a substantially constant predetermined rate of speed and in a generally linear path of travel substantially parallel to the warp yarns of the fabric and with the peaked cutting edge of the anvil and positioned so that the edge of the fabric to be sealed is passed over the first surface of the anvil;
• cutting an edge through the textile fabric substantially parallel with a warp yarn by vibrations of the sonic horn against the peaked cutting edge of the anvil;
• simultaneously sealing the cut edge of the fabric by fusing and bonding a mass of thermoplastic fibers in the fabric adjacent to and extending inwardly of the fabric from the cutting edge from about 0.02 to 0.06 inch and encompassing from about 2 to 4 of the warp yarns extending parallel to the cut edge by vibrations of the sonic horn toward the first surface of the anvil;
• and
• applying a predetermined pressure to the anvil and to the vibrating sonic horn for exerting predetermined forces on the fabric passing therebetween for aiding in the ultrasonic cutting and sealing.