Method for forming a chemical conversion phosphate film on the surface of steel
AssigneeNippondenso Co., Ltd.
InventorShigeki Matsuda
Life of this patent
Estimating the term…
Abstract
The present invention proposes a method for forming a chemical conversion phosphate film on the surface of steel, characterized in that the temperature of the conversion bath is from 0.degree. C. to 40.degree. C., the hydrogen-ion concentration (pH) of the conversion bath is in the range of from pH 2.2 to pH 3.5, and the oxidation reduction potential of the conversion bath is from 0 mV to 700 mV (normal hydrogen electrode potential). According to the present invention, normal-temperature phosphating and automatic bath control are attained.
Claims10
A method of forming a chemical conversion phosphate film on the surface of steel parts comprising the steps of:
- (a) bringing said steel parts into contact with a conversion bath containing materials participating in the chemical conversion reactions, including a conversion-coating agent, an oxyacid anions, and an oxidizer, and maintaining the conversion bath within the range of from 0.degree. C. to 40.degree. C.;
- (b) predetermining a hydrogen-ion concentration (pH) of the conversion bath in the range of from pH 2.2 to pH 3.5 and oxidation reduction potential (ORP) of the conversion bath in a range of from 0 mV to 700 mV (normal hydrogen electrode potential), so that concentrations of said materials is controlled and maintained to form said chemical conversion phosphate film on the surface of the steel parts, and further, that said pH an ORP ranges in combination with said temperature range produce, in step (a), a relationship between the concentration of said oxidizer said ORP, indicating at a given ORP value of the concentration of said oxidizer;
- (c) measuring the hydrogen-ion concentration of the conversion bath during the step (a);
- (d) measuring an oxidation reduction potential (ORP) of said conversion bath during the step (a);
- (e) replenishing a main agent containing phosphate ions, when the measured pH rises above a value predetermined within said range of pH 2.2 to 3.5;
- (f) replenishing said oxidizer, when the measured ORP decreases to less than a value predetermined within said range of 0 to 700 mV;
- (g) when, due to an increase in a relative amount of the oxyacid anions to conversion-coating agents, said measured pH value falls below a value predetermined within said range of pH 2.2 to 3.5, replenishing alkali and thereby removing the oxyacid anions by added alkali, and maintaining concentrations of said materials to form said chemical conversion phosphate film;
- (h) repeating replenishing steps (e), (f), and (g) during the step (a) as required, thereby maintaining said concentrations of materials during the chemical conversion of steel parts.
A method for forming a chemical conversion phosphate film on the surface of steel parts by a general corrosion reaction of said steel parts, said method comprising the steps of:
- (a) bringing said steel parts into contact with a conversion bath maintained within a range of from 0.degree. C. to 40.degree. C.;
- (b) maintaining the hydrogen-ion concentration (pH) of the conversion bath in the range of from pH 2.2 to pH 3.5 and maintaining the oxidation reduction potential (ORP) of the conversion bath in a range of from 0 mV to 700 mV (normal hydrogen electrode potential);
- (c) replenishing a main agent containing phosphate ions, oxyacid anions, and metal ions, when the pH rises above a value predetermined within said range of pH 2.2 to 3.5;
- (d) when the ORP decreases to less than a value predetermined within said range of 0 to 700 mV, replenishing said oxidizer in an amount determined by a relationship between the concentration between said oxidizer and said ORP, indicating at a given ORP one value of the concentration of said oxidizer;
- (e) when said pH value falls below a value predetermined within said range of pH 2.2 to 3.5, replenishing alkali.
Dependencies are inferred from the claim text.