Method of making a rim-stabilized steel ingot
AssigneeUnited States Steel Corporation
InventorsPaul E. Hamill, Jr., Robert H. Kachik
Life of this patent
Estimating the term…
Abstract
A simple method of producing a rim-stabilized steel ingot without requiring the use of special equipment wherein a rimming-type steel is teemed into an ingot mold and thereafter allowed to rim for a suitable period of time, and then adding a particulate mixture of aluminum and an exothermic material to the top of the molten metal so that the exothermic mixture will ignite, melting and superheating the aluminum content which is driven into the molten steel at the ingot core.
Claims5
A process for producing a rim-stabilized steel ingot comprising:
- (a) teeming a rimming-type steel into an ingot mold until said mold is substantially full,
- (b) allowing the teemed steel to rim in the ingot mold for a period of from 1/2 to 15 minutes,
- (c) thereafter adding an aluminum-exothermic material mixture to the top of the molten metal in the ingot mold, said mixture containing sufficient particulate aluminum as will at least semi-kill the molten steel in the ingot core and a stoichiometric blend of fuel and oxidizing agent sufficient to melt and superheat the particulate aluminum,
- (d) and allowing the heat from the molten steel in the ingot mold to ignite the exothermic mixture so that the exothermic reaction will (1) melt and superheat the particulate aluminum, (2) melt any ingot surface scum therebeneath, and (3) drive the molten, superheated aluminum into the ingot core.
1 more element
Dependencies are inferred from the claim text.