Method of producing phosphorus pentoxide in a kiln with reduced carbon burnout

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material to form a feed mixture;
• forming the feed mixture into pellets;
• coating the pellets with a silica fluxing agent;
• heating the coated pellets by exposure to radiation emanating from an oxidation zone within a kiln to a temperature enabling the silica fluxing agent to promote melting of the silica proximate to surface areas of the coated pellets to reduce oxidation of the carbonaceous material in the coated pellet by at least partially sealing coated pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the coated pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapors;
• and
• introducing into the kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the coated pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and a silica fluxing agent to form a feed mixture;
• forming the feed mixture into pellets;
• coating the pellets with a mixture comprising silica and a silica fluxing agent;
• heating the coated pellets by exposure to radiation emanating from an oxidation zone within a kiln to a temperature enabling the silica fluxing agent to promote melting of the silica proximate to surface areas of the coated pellets to reduce oxidation of the carbonaceous material in the coated pellet by at least partially sealing coated pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the coated pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapors;
• and
• introducing into the kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the coated pellets.

A process for producing phosphorous pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and a silica fluxing agent to form a feed mixture;
• forming the feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a temperature enabling the silica fluxing agent to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapors;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica solid carbonaceous material and a silica fluxing agent to form a feed mixture;
• co-grinding the phosphate ore feed mixture so that 50 to 85 percent of the co-ground feed mixture passes a -325 mesh;
• forming the co-ground feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a temperature enabling the silica fluxing agent to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapor;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphorus ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and phosphoric acid in amounts to produce a feed mixture having a phosphoric acid content of about 0.4 to about 1.0 percent by weight;
• co-grinding the feed mixture so that 50 to 85 percent of the co-ground feed mixture passes a -325 mesh;
• forming the co-ground feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a temperature enabling the silica fluxing agent to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapors, said heating of the pellets being at a rate of approximately 3.degree. to approximately 5.degree. C. per minute;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and a silica fluxing agent to form a feed mixture, said fluxing agent promoting said silica to sinter in the temperature range of 700.degree. C. to 1100.degree. C.;
• forming the feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to 1100.degree. C. enabling the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to a temperature sufficient to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapors;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and a silica fluxing agent to form a feed mixture, said fluxing agent promoting said silica to melt in the temperature range of 700.degree. C. to 1100.degree. C., said fluxing agent vaporizing at temperatures greater than about 1100.degree. C.;
• forming the feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a 1100.degree. C. enabling to the silica fluxing agent to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to at least 1300.degree. C. to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapor and vaporize the fluxing agent from the surface areas of the pellet to enable the elemental phosphorus vapors to escape the pellets and enter the oxidation zone;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material and phosphoric acid to form a feed mixture having a phosphoric acid content of about 0.4 to about 1.0 percent by weight, phosphoric acid decomposing to phosphorus pentoxide at temperatures greater than about 1100.degree. C.;
• co-grinding the feed mixture so that 50 to 85 percent of the co-ground feed mixture passes a -325 mesh;
• forming the co-ground feed mixture into pellets;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a 1100.degree. C. enabling the phosphorus pentoxide to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to at least 1300.degree. C. to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapor and drive the phosphorus pentoxide from the surface areas of the pellet to enable the elemental phosphorus vapors to escape the pellets and enter the oxidation zone;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.

A process for producing phosphorus pentoxide from phosphate ore comprising the steps of:

• mixing phosphate ore containing silica with solid carbonaceous material to form a feed mixture;
• forming the feed mixture into pellets;
• coating the pellets with a silica fluxing agent, said fluxing agent promoting said silica to melt in the temperature range of 700.degree. C. to 1100.degree. C., said fluxing agent vaporizing at temperatures greater than about 1100.degree. C.;
• heating the pellets by exposure to radiation emanating from an oxidation zone within a rotary-type kiln to a 1100.degree. C. enabling to the silica fluxing agent to promote melting of the silica proximate to surface areas of the pellets to reduce oxidation of the carbonaceous material in the pellet by at least partially sealing pellet interior portions from the oxidation zone, and thereafter continuing to heat the pellets to at least 1300.degree. C. to reduce the phosphate in the pellets by reaction with the solid carbonaceous material to form elemental phosphorus vapor and vaporize the fluxing agent from the surface areas of the pellet to enable the elemental phosphorus vapors to escape the pellets and enter the oxidation zone;
• and
• introducing into the rotary-type kiln sufficient oxygen-containing gas to cause oxidation of the elemental phosphorus vapor within the oxidation zone to produce phosphorus pentoxide and to heat the pellets.