Rejuvenation of the anion exchanger used for uranium recovery
AssigneeMobil Oil Corporation
InventorsTsoung-Yuan Yan, Wilton F. Espenscheid
Life of this patent
Estimating the term…
Abstract
A process is described for restoring and maintaining the total ion exchange capacity of the resin used for uranium recovery in in situ uranium leaching. The used resin of lowered exchange capacity is treated with a solution containing Na.sub.2 CO.sub.3 or NaHCO.sub.3, or admixtures thereof. The process preferably is used in conjunction with acid elution of the uranium from the resin.
Claims5
A process for restoring the ion exchange capacity of a strong base anion exchange resin used for recovering uranium, in the form of uranyl carbonate anions, from solutions used to leach uranium from subterranean formations which comprises:
- treating the resin with acid to elute uranium values therefrom;
- washing the resin with a solution containing 0.5 to 100 grams/liter of sodium carbonate, sodium bicarbonate, or admixtures thereof, for a time sufficient to substantially free the resin of materials which are either soluble in said solution or react with said solution.
A process for isolating uranium which has been leached from subterranean formations by a leach solution containing carbon dioxide and oxygen wherein said leach solution has been contacted with a strong base anion exchange resin so that uranium contained in the leach solution is exchanged on said resin and for substantially restoring to said resin its original total ion exchange capacity prior to being contacted with said leach solution which comprises:
- eluting the resin with hydrochloric acid to remove uranium in the form of uranyl carbonate anions, and
- contacting the resin with a solution of sodium carbonate, sodium bicarbonate, or admixtures thereof for a time sufficient to substantially restore said total ion exchange capacity.
An improved process for the recovery of uranium values from a uranium-containing lixiviant, utilizing a strong base anion exchange resin, comprising the steps of:
- (a) passing the uranium-containing lixiviant through the strong base anion exchange resin to cause said resin to retain uranium values;
- (b) eluting the resin with hydrochloric acid to remove uranium values therefrom;
- (c) repeating steps (a) and (b) until total uranium loading capacity of the resin is substantially reduced.
- (d) washing the resin with a solution of sodium carbonate, sodium bicarbonate, or admixtures thereof for a time sufficient to restore said total uranium loading capacity;
- and
- (e) recycling the restored resin for utilization in step (a).
Dependencies are inferred from the claim text.