Lubricating composition and method for making
OwnerSal A. Randisiinventor
Life of this patent
Estimating the term…
Abstract
A lubricating composition is provided which is a stable dispersion of a lubricating fluid such as a natural or synthetic petroleum distillate, and a finely divided polymeric fluorocarbon powder such as polytetrafluoroethylene such as Teflon and a silicon dioxide powder such as a fumed silica. The composition is best provided by utilization of a disc impeller at elevated temperature to attain a moisture-free, even dispersion of the Teflon and the silica in the fluid. The lubricating composition is particularly useful in wide temperature range service, particularly so at extremely high and low temperatures.
Claims19
A lubricating composition useful for wide temperature range service, said lubricating composition having a service temperature range from about -72.degree. F. to about 500.degree. F. and an electrical resistance ranging from about 1.times.10.sup.14 Ohm-cm to about 2.times.10.sup.14 Ohm-cm at 100 volts, said lubricating composition comprising a stable dispersion of:
- a. a hydrocarbon lubricating liquid, said hydrocarbon liquid comprising from about 50% to about 95% of said lubricating composition;
- b. a finely divided polymeric fluorocarbon powder comprising polytetrafluoroethylene in the form of a finely divided powder with particles ranging from about 0.1 to 100 microns in size and having a melting temperature above 450.degree. F., said polymeric fluorocarbon powder comprising from about 1% to about 3% of said lubricating composition, and;
- c. a silicon dioxide in the form of a finely divided fumed silica powder with particles ranging from about 7 to about 40 millimicrons in size, said silicon dioxide comprising from about 2% to about 10% of said lubricating composition.
A method for making a lubricating composition useful for wide temperature range service, said lubricating composition being a stable dispersion and having a service temperature range from about -72.degree. F. to about 500.degree. F. and an electrical resistance ranging from about 1.times.10.sup.14 Ohm-cm to about 2.times.10.sup.14 Ohm-cm at 100 volts, said method comprising:
- a. providing a hydrocarbon lubricating liquid, said hydrocarbon liquid comprising from about 50% to about 95% of said lubricating composition;
- b. adding and mixing into said hydrocarbon liquid finely divided polymeric fluorocarbon particulates in a first mixing step, said polymeric fluorocarbon particulates comprising polytetrafluoroethylene in the form of a finely divided powder with particles ranging from about 0.1 to 100 microns in size and having a melting temperature above 450.degree. F., said polymeric fluorocarbon powder comprising from about 1% to about 3% of said lubricating composition, and
- c. subsequently adding to the hydrocarbon liquid-polymeric fluorocarbon powder mixture produced by step (b), and mixing into said mixture in a second mixing step, finely divided silicon dioxide particulates in the form of a finely divided fumed silica powder with particles ranging from about 7 to about 40 millimicrons in size, said silicon dioxide particulates comprising from about 2% to about 10% of said lubricating coposition;
- said first and second mixing steps being carried out by contacting said components with a rotating disc impeller, so as to provide evenly dispersed particulates of both said polymeric fluorocarbon powder and said silicon dioxide powder in said hydrocarbon lubricating liquid.
Dependencies are inferred from the claim text.