Hydrodesulfurization catalyst on lithium-containing support and method for its preparation
AssigneeUnion Oil Company of California
InventorsJ. Wayne Miller, Howard D. Simpson
Life of this patent
Estimating the term…
Abstract
The porosity and surface area of refractory oxides are modified by adding a lithium component thereto and then calcining. The resultant material, having a lower surface area, a lower total pore volume, and a larger average pore diameter in comparison to the original refractory oxide, is highly useful as a catalyst support, particularly with respect to hydrodesulfurization catalysts.
Claims34
A method for preparing a catalyst which method comprises incorporating a porous refractory oxide with a lithium component, calcining the lithium-incorporated porous refractory oxide to form a lithium component-containing composition having a substantially increased average pore diameter than that of said porous refractory oxide and incorporating a Group VIB metal component with said composition.
A method for preparing a hydroprocessing catalyst containing a precalcined porous refractory oxide comprising gamma alumina which method comprises incorporating said precalcined porous refractory oxide with a lithium component, calcining the lithium-incorporated porous refractory oxide at a temperature greater than about 1,200.degree. F. to produce a lithium component-containing composition having an increased average pore diameter between about one and about four times that of said precalcined porous refractory oxide and incorporating a Group VIB metal component with said composition.
A method for producing a lithium-containing composition, said method comprising the steps of:
- (1) incorporating a lithium component with a porous refractory oxide,
- (2) calcining the lithium-incorporated refractory oxide produced in step (1) at a temperature of about 1400.degree. F. to about 1600.degree. F.,
- (3) contacting the calcined lithium-incorporated refractory oxide obtained in step (2) with Group VIB metal in Group VIII metal hydrogenation components, and
- (4) calcining the composition obtained from step (3) to produce a catalytic composition comprising Group VIB and Group VIII metals and lithium on a porous refractory oxide, said catalytic composition having an increased average pore diameter between about one and about four times that of said porous refractory oxide.
A catalytic composition prepared by a method comprising incorporating a porous refractory oxide with a lithium component, calcining the resultant lithium-incorporated porous refractory oxide at an elevated temperature to form a lithium component-containing composition having an increased average pore diameter than that of said porous refractory oxide and incorporating a Group VIB metal component with said calcined lithium component-containing composition.
A catalytic composition prepared by the method comprising the steps of:
- (1) incorporating a porous refractory oxide comprising alumina with a lithium component containing a thermally decomposable anion,
- (2) calcining the lithium-incorporated porous refractory oxide at a temperature of about 1400.degree. F. to about 1600.degree. F.,
- (3) contacting the resultant lithium-incorporated porous refractory oxide obtained from step (2) with a Group VIB metal and a Group VIII metal hydrogenation component, and
- (4) calcining the composition of step (3) to produce a catalytic composition having an increased average pore diameter between about one and about four times that of said porous refractory oxide.
A catalytic composition comprising at least one group VIB metal hydrogenation component and at least one Group VIII metal component, and a porous refractory oxide containing between about 0.1 and about 10 weight percent of lithium components, calculated as Li, and wherein said composition is prepared by the method comprising the steps of:
- (1) incorporating a porous refractory oxide with a lithium component,
- (2) calcining the lithium-incorporated porous refractory oxide at an elevated temperature to produce a lithium component-containing composition having a substantially increased average pore diameter than that of said porous refractory oxide, and
- (3) incorporating at least one Group VIB metal hydrogenation component with said composition obtained from step (2).
A catalytic composition useful for hydrodesulfurization of hydrocarbon oils comprising Group VIB and Group VIII metals on an alumina-containing porous refractory oxide comprising at least about 0.1 weight percent of lithium, calculated as Li, said composition prepared by the method comprising the steps of:
- (1) incorporating a porous refractory oxide with a lithium component,
- (2) calcining the lithium-incorporating porous refractory oxide at a temperature greater than about 1,200.degree. F. to produce a lithium component-containing composition having an increased average pore diameter between about one and about four times that of said porous refractory oxide, and
- (3) incorporating at least one Group VIB and at least one Group VIII metal hydrogenation component with said composition obtained from step (2).
The composition defined in claim 17, 18, 29 or 41 wherein said increased average pore diameter is about two to about three times that of said porous refractory oxide.
The composition defined in claims 17, 18, 29 or 41 further comprising an average pore diameter in the range between about 100 and about 250 angstroms.
The composition defined in claim 17, 18, 29 or 41 wherein said Group VIB metal is molybdenum.
The composition defined in claim 17, 18, 29 or 41 further comprising a total pore volume between about 0.30 and about 1.0 cc/gram.