Method of making a bearing material containing an aluminum base alloy
AssigneeNDC Company, Ltd.
InventorsYoshitsugu Kanda, Minoru Kurikawa, Toru Morimoto, Kiyoshi Nakanishi
Life of this patent
Estimating the term…
Abstract
In the manufacture of a bearing material containing an aluminum base alloy, one surface of a steel strip is washed and roughened; the aluminum base alloy is spread on the surface of the steel strip; and the aluminum base alloy and the steel strip are hot-rolled in the air to pressure-bond the former to the latter into a unitary structure. Prior to spreading the aluminum base alloy, an aluminum powder which well adheres to the steel strip may also be spread on the surface of the steel strip.
Claims2
A method of making an aluminum base alloy bearing material, comprising the steps of:
- (a) washing one surface of a continuously fed steel strip or stainless steel strip;
- (b) grinding the resulting washed surface of the strip;
- (c) spreading on the resulting ground surface of the strip an aluminum base alloy powder containing from 6.8 to 9.2 wt % lead and from 0.8 to 1.5 wt % tin, to form an aluminum base alloy powder on the surface of the strip;
- (d) preheating the strip having the aluminum base alloy powder thereon by the application of heat to the other surface of the strip to a temperature in the range of from 200.degree. C. to 400.degree. C., in an air atmosphere, without directly heating the aluminum base alloy;
- (e) hot-rolling the preheated strip and the aluminum base alloy in the air atmosphere between a pair of heated rolls, each heated up to from 150.degree. C. to 400.degree. C. over the entire area of the surface thereof, to thereby pressure-bond the aluminum base alloy powder to the strip to form thereon a bearing surface layer;
- (f) taking up the resulting bearing steel strip into a coil;
- and
- (g) heating the coil in a furnace to sinter the coating at a temperature of from 250.degree. C. to 500.degree. C.
A method of making an aluminum base alloy bearing material, comprising the steps of:
- washing and roughening one surface of a continuously fed steel strip;
- spreading on the surface of the steel strip an aluminum powder consisting essentially of aluminum;
- spreading an aluminum base alloy powder on the aluminum powder;
- and
- hot-rolling the aluminum powder, the aluminum base alloy powder and the steel strip to pressure-bond the powders to the steel strip into a unitary structure.
Dependencies are inferred from the claim text.