Rapidly dissolvable silicates and methods of using the same
AssigneeHalliburton Company
InventorJoseph R. Murphey
Life of this patent
Estimating the term…
Abstract
Rapidly dissolvable powdered silicates having a molar ratio of silicon dioxide to alkali metal oxide in the range of from about 1.5:1 to about 3.3:1 wherein the alkali metal is selected from the group consisting of sodium, potassium and mixtures thereof. Methods of using the powdered silicates and resulting solutions in connection with sealing and cementing, especially of well formations, are provided.
Claims5
A method of sealing a lost circulation zone during drilling operations in an earth formation where due to lack of storage area for or low temperatures sufficient to freeze liquid potassium silicate such solutions are unavailable and where said formation contains di- or polyvalent cations or salts, comprising the steps of:
- preparing a potassium silicate solution by mixing water with a highly dissolvable partially hydrated powdered amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1 and a water content in the range of from about 14% to about 16% by weight of said partially hydrated potassium silicate said solution being of a type which will gel when combined with di- or polyvalent cations or salts of the type in the earth formation and will penetrate the formation without premature floculation and gelation;
- introducing the prepared potassium silicate solution into the earth formation;
- and
- allowing the potassium silicate solution to gel into a relatively firm impermeable mass thereby sealing the formation.
A method of sealing a vugular, matrix or channel earth formation comprising the steps of:
- combining water with a cementitious mixture of cement powder and a rapidly dissolvable partially hydrated powdered amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1 and a water content in the range of from about 14% to about 16% by weight of said partially hydrated potassium silicate;
- introducing the resultant solution into the formation;
- and
- allowing the potassium silicate solution to gel thereby sealing the vugular, matrix or channel portions of the earth formation.
An improved method of sealing or cementing an earth formation of the type utilizing a silicate solution prepared at the site of such sealing or cementing operations from a rapidly dissolvable partially hydrated powder silicate, the improvement comprising the steps of:
- preparing said silicate solution at the earth formation location by dissolving a rapidly dissolvable partially hydrated, powdered silicate having a molar ratio of silicon dioxide to alkali metal oxide in the range of from about 1.5:1 to about 3.3:1 and wherein said alkali metal is selected from the group consisting of sodium, potassium and mixtures thereof;
- and
- utilizing the resulting solution in said sealing or cementing method.