Process for calcining and desulfurizing petroleum coke
AssigneeGreat Lakes Carbon Corporation
InventorsHarry L. Hsu, Edward E. Hardin, Lloyd I. Grindstaff
Life of this patent
Estimating the term…
Abstract
Low sulfur calcined coke having an adequate density value for industrial consumers is produced from high sulfur raw coke by treating the coke in three heating stages under controlled conditions, one of the stages being in the presence of added hydrogen.
Claims3
A process for producing calcined petroleum coke having a sulfur content in the range of about 1.8 to about 2.5 wt. % and a vibrated bulk density of at least about 78 g/100 cc from raw petroleum coke having a sulfur content of at least about 3.5 wt. % an a volatile content of at least about 7 wt. % which comprises:
- (a) heating the coke at a temperature in the range of about 600.degree. C. to about 800.degree. C. in the absence of added hydrogen for a time sufficient to reduce the volatile content of the coke to a value in a range of about 3 to about 6 wt. %;
- (b) heating the partially devolatilized coke at a temperature in the range of about 600.degree. C. to about 800.degree. C. in an atmosphere containing added hydrogen for a period of time sufficient to reduce the sulfur content of said coke to a level in the range of about 2.8 to about 3.3 wt. %;
- and
- (c) heating the partially desulfurized coke at a temperature in the range of about 1350.degree. C. to about 1600.degree. C. in the absence of added hydrogen for a period of time sufficient to reduce the sulfur content of the coke to within the range of about 1.8 to about 2.5. wt. %.
A process for producing calcined petroleum coke having a sulfur content in the range of about 1.8 to about 2.5 wt. % and a vibrated bulk density of at least about 78 g/100 cc from raw petroleum coke having a sulfur content in the range of about 3.5 to about 5.0 wt. % and a volatile content in the range of about 9 to about 14 wt. % which comprises:
- (a) heating the coke at a temperature in the range of about 600.degree. C. to about 800.degree. C. in the absence of added hydrogen for a period of time of about 1 hour to about 2 hours such that the volatile content of the coke is reduced to a value in the range of about 3 to about 6 wt. %;
- (b) heating the partially devolatilized coke at a temperature in the range of about 600.degree. C. to about 800.degree. C. for a period of time of about 3 hours to about 6 hours in an atmosphere containing added hydrogen such that the sulfur content of said coke is reduced to a level in the range of about 2.8 to about 3.3 wt. %;
- and
- (c) heating the partially desulfurized coke at a temperature in the range of about 1350.degree. C. to about 1600.degree. C. in the absence of added hydrogen for a period of time of about 0.5 hour to about 1.5 hours such that the sulfur content of the coke coke is reduced to a level of about 1.8 to about 2.5 wt. %.
Dependencies are inferred from the claim text.