Loading patent…
AssigneeBethlehem Steel Corporation
InventorsLouis K. Allegra, Herbert E. Townsend, Angelo R. Borzillo
Estimating the term…
This invention relates to an aluminum-zinc alloy coated ferrous base product which exhibits improved atmospheric corrosion resistance, and to the process whereby such improved corrosion resistance may be realized. The process is characterized by the steps of heating such coated product to a temperature within the single phase region for the composition corresponding to the aluminum and zinc of said coating, defined as .alpha. in the FIGURE in the accompanying drawing, preferably at a temperature between about 650.degree. F. (343.degree. C.) to 750.degree. F. (399.degree. C.), for a period of time to solution treat the aluminum-zinc alloy coating overlay, and cooling slowly to at least 350.degree. F. (177.degree. C.). The resulting product is characterized by improved atmospheric corrosion resistance as a result of the combination of an aluminum-zinc alloy coating overlay having a structure comprised of a fine dispersion of beta-zinc within a matrix of alpha-aluminum, and a thin intermetallic layer interposed between said overlay and said ferrous base.
A method of treating an as-cast, hot-dipped aluminum-zinc alloy coated ferrous product to improve the atmospheric corrosion behavior of the coating by altering its corrosion mechanism from a preferential corrosion of the continuous, zinc-rich interdentritic constituent to a uniform corrosion of the aluminum-rich matrix having within it a discontinuous zinc-rich phase, said as-cast coating comprising, by weight, 25 to 70% aluminum, balance essentially zinc with a small addition of silicon, and a structure having (1) an alloy overlay of cored aluminum-rich dendrites and zinc-rich interdendritic constituents, and (2) an intermetallic layer intermediate said overlay and the ferrous base, characterized by the steps of heating said coated ferrous product to a temperature within the single phase region for the composition of said aluminum-zinc alloy, defined as .alpha. in FIG. 1 in the accompanying drawings, for a sufficient time to cause dissolution of said interdendritic zinc-rich constituents in said alloy coating overlay, and cooling slowly to about 350.degree. F. (177.degree. C.), whereby to produce a coating overlay structure comprising a fine dispersion of zinc within an aluminum-rich matrix.
A method of producing an aluminum-zinc alloy coated ferrous product to improve the atmospheric corrosion behavior of the coating by altering its corrosion mechanism, characterized by the steps of coating said ferrous product with molten aluminum-zinc alloy comprising, by weight, 25 to 70% aluminum, balance essentially zinc with a small addition of silicon, cooling said aluminum-zinc alloy coating during substantially the entire solidification of said coating at a rate of at least 20.degree. F./sec. (11.degree. C./sec.) to produce an aluminum-zinc alloy coating comprising (1) an alloy overlay of cored aluminum-rich dendrites and zinc-rich interdentritic constituents, and (2) an intermetallic layer intermediate said overlay and the ferrous base, arresting said cooling and holding said coated ferrous product at a temperature within the single phase region for the composition of said aluminum-zinc alloy, defined as .alpha. in FIG. 1 in the accompanying drawings, for a sufficient time to cause dissolution of said interdendritic zinc-rich constituents in said alloy coating overlay, and cooling the coated ferrous product slowly to about 350.degree. F. (177.degree. C.), whereby to produce a coating overlay structure of a fine dispersion of zinc within an aluminum-rich matrix.
Dependencies are inferred from the claim text.