Peroxide treated substantially amorphous polyolefin/hydrocarbon rubber blends useful as pressure-sensitive adhesives

A process for preparing tacky modified amorphous polyolefin/hydrocarbon rubber compositions useful as pressure sensitive adhesives which comprises reacting a blend comprising at least one hydrocarbon rubber selected from the group consisting of ethylene/propylene copolymer rubber, ethylene/propylene/diene terpolymer or blends of such hydrocarbon rubbers and up to 50 weight percent of at least one substantially amorphous polyolefin selected from the group consisting of substantially amorphous homopolymers of 1-olefins containing 3 to 5 carbon atoms, substantially amorphous copolymers prepared from either ethylene and 1-olefins containing 3 to 5 carbon atoms or propylene and 1-butene, and substantially amorphous propylene or 1-butene/higher 1-olefin copolymers containing less than 40 mole percent of at least one higher 1-olefin of the group consisting essentially of 1-hexene, 1-heptene, 1-octene, 1-nonene, and 1-decene having a melt viscosity of about 100 to 200,000 cp. at 190.degree. C. with about 3 to 20 weight percent of at least one peroxide selected from the group consisting of ditertiarybutyl peroxide, 2,5-dimethyl-2,5-di(tertiarybutylperoxy)hexane, dicumyl peroxide, and cumene hydroperoxide at a temperature of 150.degree. C. to 250.degree. C. to provide a low viscosity, permanently tacky hot-melt pressure sensitive adhesive.

A process for preparing tacky modified amorphous polyolefin/hydrocarbon rubber compositions useful as pressure sensitive adhesives which comprises reacting a blend comprising at least one hydrocarbon rubber selected from the group consisting of ethylene/propylene copolymer rubber, ethylene/propylene diene terpolymer or blends of such hydrocarbon rubbers and up to 50 weight percent of at least one substantially amorphous polyolefin selected from the group consisting of substantially amorphous homopolymers of 1-olefins containing 3 to 5 carbon atoms, substantially amorphous copolymers prepared from either ethylene and 1-olefins containing 3 to 5 carbon atoms or propylene and 1-butene, and substantially amorphous propylene or 1-butene/higher 1-olefin copolymers containing less than 40 mole percent of at least one higher 1-olefin of the group consisting essentially of 1-hexene, 1-heptene, 1-octene, 1-nonene, and 1-decene having a melt viscosity of about 100 to 200,000 cp. at 190.degree. C. with about 3 to 20 weight percent of at least one peroxide selected from the group consisting of ditertiarybutyl peroxide, 2,5-dimethyl-2,5-di(tertiarybutylperoxy)hexane, dicumyl peroxide, and cumene hydroperoxide at a temperature of 175.degree. C. to 225.degree. C. to provide a low viscosity, permanently tacky hot-melt pressure sensitive adhesive.

A process for preparing tacky modified amorphous polyolefin/hydrocarbon rubber compositions useful as pressure sensitive adhesives which comprises reacting a blend comprising at least one hydrocarbon rubber selected from the group consisting of ethylene/propylene copolymer rubber, ethylene/propylene/diene terpolymer or blends of such hydrocarbon rubbers and up to 50 weight percent of at least one substantially amorphous polyolefin selected from the group consisting of substantially amorphous homopolymers of 1-olefins containing 3 to 5 carbon atoms, substantially amorphous copolymers prepared from either ethylene and 1-olefins containing 3 to 5 carbon atoms or propylene and 1-butene, and substantially amorphous propylene or 1-butene/higher 1-olefin copolymers containing less than 40 mole percent of at least one higher 1-olefin of the group consisting essentially of 1-hexene, 1-heptene, 1-octene, 1-nonene, and 1-decene having a melt viscosity of about 100 to 200,000 cp. at 190.degree. C. with about 3 to 20 weight percent of at least one peroxide selected from the group consisting of ditertiarybutyl peroxide, 2,5-dimethyl-2,5-di(tertiarybutylperoxy)hexane, dicumyl peroxide, and cumene hydroperoxide at a temperature of about 200.degree. C. to provide a low viscosity, permanently tacky hot-melt pressure-sensitive adhesive.