Abstract
An adhesive composition and process for making the same are disclosed wherein the adhesive composition has greatly improved high temperature properties. The adhesive composition is prepared by first melt blending a polyphenylene ether resin and a low molecular weight resin, and then blending the resulting mixture with a monoalkenyl arene/conjugated diene block copolymer, tackifying resin, and optional hydrocarbon processing oil.
Claims9
A hot melt adhesive composition comprising:
- (a) 100 parts by weight of a block copolymer having at least two monoalkenyl arene polymer end blocks A and at least one elastomeric conjugated-diene mid-block B, said blocks A comprising 8 - 55% by weight of the block copolymer;
- (b) about 50 to about 200 parts by weight of a tackifying resin compatible with block B;
- (c) about 0 to about 200 parts by weight of a hydrocarbon extending oil;
- and
- (d) about 5 to about 50 parts by weight of a melt blend of
- (i) a low molecular weight polyphenylene ether resin, and
- (ii) a block A compatible resin selected from the group consisting of coumarone-indene resins, vinyltoluene-alphamethyl-styrene copolymers and mixtures thereof, wherein the weight ratio of the polyphenylene ether resin to the block A compatible resin is between about 1:1 and about 1:6, the molecular weight (M.sub.vis) of the polyphenylene ether resin is between about 6,000 and about 25,000, the glass transition temperature of the polyphenylene ether resin is between 170.degree. C and 205.degree. C;
- and the glass transition temperature of the block A compatible resin is between about 40.degree. C and about 100.degree. C.
A hot melt adhesive composition prepared by melt blending various components at a temperature of between 175.degree. and 180.degree. C and in the absence of a solvent wherein the various components consist of:
- a. 100 parts by weight of a block copolymer having at least two styrene polymer end blocks A and at least one isoprene midblock B, said blocks A comprising 8 - 55% by weight of the block copolymer;
- b. 125 parts by weight of a tackifying resin compatible with block B;
- c. 25 parts by weight of a hydrocarbon extending oil;
- and
- d. 35 parts by weight of a melt blend of
- (i) a low molecular weight poly(2,6 -dimethyl-1,4-phenylene) ether resin, and
- (ii) a coumarone-indene resin having a glass transition temperature of about 88.degree. C, wherein the weight ratio of the polyphenylene ether resin to coumarone-indene resin is 25:75, the molecular weight (M.sub.vis) of the polyphenylene ether resin is about 10,400 and its glass transition temperature is about 195.degree. C.