Cementitious coatings and method
OwnerCharles E. Cornwell, Mark Plunguianinventors
Life of this patent
Estimating the term…
Abstract
Protective and decorative coatings of about two mills and greater thickness are produced from hydraulic cement slurries formulated with finely divided mineral aggregates, a film-forming synthetic polymer latex, a "super" water reducer, and a rust inhibitor. These constituents are formulated into liquid and powder components which are mixed prior to spraying or brushing to produce the coating. The coatings are non-burning and are applicable for interior and exterior use. Very fast set of the cement are obtainable by admixing an accelerator to either the liquid or powder component and mixing the two components continuously by passing through a static in-line mixing device located in a feed line duct just before a spray nozzle.
Claims8
A coating of about 2 mils to about 60 mils thickness of an hydraulic cement composition which comprises in weight percent a dry component of mineral cement selected from the group of portland and calcium aluminate cement, 100;
- a mineral aggregate of 100 mesh or finer selected from the group of calcite and silica and mixtures thereof, 15-60;
- pozzolonic fly ash, 0-15;
- calcium stearate, 0-1;
- color pigments, 0-5;
- and a cement accelerator, 0-3;
- and a liquid component to be admixed to the dry component, of water, 35-50;
- a synthetic polymer latex selected from the group of polymers which are film-forming at ambient temperature, 5-30, with an equivalent polymer solids of 2.5-16;
- a super water reducer selected from the group of polymers comprising the alkali metal salts of melamine sulfonic acid partially condensed with formaldehyde, the alkali metal salt of naphthalene sulfonic acid partially condensed with formaldehyde, and about 30-90 percent of the alkali metal salt of a high molecular weight condensation product of naphthalene-sulfonic acid and the balance 70-10 percent being the alkali salt of gluconic acid, 0.5-3.0;
- sodium nitrite, 0.1-0.3;
- a cement accelerator, on a dry basis, 0-3;
- and a cement retarder, 0.05-0.5.
A process for the preparation of an improved coating of about 2 mils to about 60 mils thickness suitable for spray application, containing hydraulic cement, which comprises intermixing, in parts by weight, a blended dry component of hydraulic cement, 100, finely divided mineral aggregate, 15-60, pozzolonic fly ash, 0-15, calcium stearate, 0-1.0, and color pigments, 0-5, with a liquid component of water, 35-50, a synthetic polymer latex, 5-30, with equivalent polymer solids, 2.5-16, a super water reducer, 0.5-3.0, sodium nitrite, 0.1-0.3, and a cement retarder, 0.15-0.5, and placing the resulting mixture on a substrate until it sets.
Dependencies are inferred from the claim text.