Moisture absorption film layered product

A photocurable resin composition, comprising at least:

• a trifunctional or more (meth)acryl monomer (A) having no ethylene-oxide-modified (meth)acryloyl group;
• a trifunctional or more (meth)acryl monomer (B) having at least three ethylene-oxide-modified (meth)acryloyl groups;
• a hydroxyalkyl (meth)acrylate (C);
• and
• a photo-initiator as essential components,
• relative to 100 parts by weight of a total of the (A), the (B), and the (C),
• a content of the (A) is 1 to 20 parts by weight,
• a content of the (B) is 30 to 59 parts by weight, and
• a content of the (C) is 40 to 69 parts by weight,
• a moisture absorption film has a water absorption rate of 10 w % or more and 30 w % or less, the moisture absorption film being produced by irradiating the photocurable resin composition with active energy ray under conditions of an illuminance within a wavelength region of 320 to 390 nm of 200 to 900 mW/cm2 and an integrated light quantity of 1000 to 8000 mJ/cm2, and
• the moisture absorption film produced on glass so as to have a thickness of 5 μm or more and 25 μm or less has a haze changing value ΔH before and after a Taber abrasion test of 4 or less.