Resin-coated metal sheet and method of producing same

Abstract

Provided is a resin-coated metal sheet that excels in adhesion, coverability, impact resistance after retort processing, and content extractability. The resin-coated metal sheet includes a metal sheet and a first resin coating layer composed of a biaxially stretched film containing polyester resin formed on one surface selected from front and back surfaces of the metal sheet. The polyester resin contains 90 mol % or more of ethylene terephthalate. The first resin coating layer has a peak intensity ratio I1725/I1615 of 0.50 to 0.65, which is a ratio of C═O peak intensity at 1725±5 cm−1 to C═C peak intensity at 1615±5 cm−1 obtained by Raman spectroscopy. The peak intensity ratio I1725/I1615 after subjecting the resin-coated metal sheet to retort processing at 130° C. for 90 min is 0.55 to 0.75. The first resin coating layer includes a wax-containing layer containing 0.1 mass % to 2.0 mass % of wax compound.