Preparation and application methods for carbosilane based polymer soil conditioner capable of enhancing stress resistance of crops

A preparation method for a carbosilane based polymer soil conditioner capable of enhancing stress resistance of crops, comprising the following steps:

• (1) taking 20-30 mass parts of straws crushed into powder, 1-5 mass parts of methyl-silicone oil as branched monomers, 1-2 mass parts of urea as an activator, and 10-20 parts of N,N-dimethylformamide as a reaction solution;
• mixing thoroughly;
• standing under room temperature conditions for 5-8 h to make the methyl-silicone oil fully permeate into the cellulose hydroxyl surface of the straw powder;
• obtaining a natural reticular branched macromolecular complex containing the silicone oil through a hydrogen bond protection effect formed by urea amino and the branched monomers;
• then, successively adding 1-2 mass parts of potassium hydroxide for adjusting the pH of the reaction solution, 5-10 mass parts of potassium thiosulfate as a reducing agent, and 1-2 mass parts of ammonium persulfate as an initiator and an oxidant;
• stirring thoroughly;
• conducting grafting and polymerization reactions under the conditions of 30-50° C. for 10-15 h;
• and after standing, conducting solid-liquid separation to obtain carbon and silicon-based natural polymer material a with functions of water retention and salt absorption;
• (2) taking 20 mass parts of calcium lignosulphonate, 1-5 mass parts of urea as crosslinking agents, 5-10 mass parts of ferrous sulfate cation exchangers, and 50-100 mass parts of distilled water in a reactor;
• stirring to fully react under the conditions of 50-80° C. for 20-30 h to fully exchange calcium lignosulphonate and ferrous sulfate cations to form lignin ferric salt;
• meanwhile, forming hydrogen bonding by the urea amino with benzene-containing hydroxyl on lignin, thereby prepolymerizing to obtain a complex of iron lignin and calcium lignosulphonate with large molecular chains;
• then, successively adding 1-10 mass parts of polyacrylamide monomers, 1-5 mass parts of ammonium persulfate as an initiator, 10-50 parts of bentonite as a pore-forming agent, and 5-10 mass parts of polyvinyl alcohol as crosslinking agents;
• stirring constantly to completely dissolve the materials;
• under the conditions of 30-80° C., standing for conducting a polymerization reaction for 10-24 h;
• forming hydrogen bonds by hydroxyl on the complex of iron lignin and calcium lignosulphonate with amino on the polyacrylamide monomers;
• and meanwhile, under the action of the initiator and the crosslinking agents, forming macromolecular chains to obtain a viscous mixed solution b with the function of water retention;
• (3) under room temperature conditions, thoroughly stirring and mixing 20 mass parts of the carbon and silicon-based natural polymer material a and 20 mass parts of the viscous mixed solution b prepared above;
• successively adding 1-2 mass parts of manganese sulfate and 1-5 mass parts of zinc sulfate and stirring thoroughly;
• adding distilled water to make the above liquid exactly reach 1000 mass parts;
• conducting an oscillatory reaction under the room temperature conditions for 15-48 h;
• standing for 10-15 h;
• and conducting solid-liquid separation and natural drying to obtain the carbosilane based polymer soil conditioner which has the functions of salt absorption and water retention and is capable of enhancing stress resistance of crops.