US 2026/0042708 A1 · PROCESS FOR PREPARING WET CONCRETE COMPOSITIONS AND A METHOD FOR CONTROLLING MIXABILITY, RHEOLOGY AND/OR OPEN TIME OF WET CONCRETE COMPOSITIONS

Abstract

A process for preparing a wet concrete composition, including mixing with water: aggregate(s), a binder system, which is 400 Kg per m3 or less of the wet concrete composition, and an admixture formulation. The binder system is prepared before or during the mixing, from at least some of the different components of the binder system, taken separately and/or in premix form(s). The binder system has between 1% and 34% dry weight of lime source(s), between 5% and 75% dry weight of ground granulated blast furnace slag, between 21% and 90% dry weight of filler(s), and between 0.1% and 5% SO3 dry weight, relative to the lime source(s), slag and filler(s). The admixture formulation includes at least one water reducing polymer, optionally with a wetting agent and/or surfactant. The mixing is carried out at a water to binder system weight ratio between 0.2 and 0.4.

Claims10

Dependent claims

1-10. (canceled)

A process for preparing a wet concrete composition comprising a step of mixing with water:

(A) at least one aggregate,
(B) a binder system, in an amount of 400 Kg per m3 of the wet concrete composition or less,
(C) an admixture formulation,
the binder system (B) being prepared before the mixing step or in situ during the mixing step, from at least some of the different components of the binder system;
said components being taken separately and/or under the form of premix(es), wherein the binder system (B) comprises:
(B1) between 1% and 34% in dry weight of at least one lime source;
(B2) between 5% and 75% in dry weight of ground granulated blast furnace slag;
(B3) between 21% and 90% in dry weight of at least one filler;
and
(B4) between 0.1% and 5% in dry weight, relative to the total weight of components (B1), (B2), and (B3), of SO3;
said ground granulated blast furnace slag being a particles mixture of particles having a d50 greater than or equal to 5 μm and less than 15 μm, and optionally between 0.1% in weight, in respect with the total weight of the ground granulated blast furnace slag and 100% of particles having a d50 between 1 μm and less than 5 μm.
said at least one filler being a particles mixture of particles having a d50 greater than or equal to 0.05 μm and less than 8 μm, and optionally between 0.1% and 50% in weight, in respect with the total weight of the filler of particles having a d50 greater than or equal to 8 μm and less than 200 μm,
measurement of d50 being done by Laser diffraction analysis by means of Laser diffraction analyzer with a humid way method,
wherein said admixture formulation (C) comprises:
(C1) at least one water reducing polymer;
(C2) optionally a wetting agent and/or a surfactant;
said water reducing polymer (C1) being a polyethylene glycol bearing terminal phosphonate groups and/or a copolymer comprising the following monomeric units:
wherein:
represents a bonding site of a monomeric unit
the quantity of monomeric units UA is between 0 and 40 mol %,
the quantity of monomeric units UB is between 25 and 95 mol %,
the quantity of monomeric units UC is between 5 and 50 mol %,
the quantity of monomeric units UD is between 0 and 25 mol %,
R1 and R2 are independently hydrogen or methyl,
Z1 is a bond, a methyl or an ethyl,
Z2 is a bond, —CH2CH2O—, —CH2CH2OCH2CH2O— or —CH2CH2CH2CH2O—
R3 is —(CH2CH2O)m—R4, —(CH(CH3)CH2O)n—R4 or —(CH2CH2OCH(CH3)CH2O)y—R4,
m, n and y being an integer independently comprised between 7 and 100,
R4 is hydrogen, methyl,
R5 is hydrogen, methyl or —CH2COOH, and
R6 is —OH, —OCH2OH, —OCH2CH2OH, —OCH2CH2CH2OH, —OCH2CH(CH3)CH2OH, —OCH2CH2CH2CH2OH, —NHR7, a group bearing a phosphate function, a group bearing phosphonate function or a group bearing sulfonate function,
R7 being a saturated or unsaturated, linear or branched chain comprising from 2 to 12 carbon atoms and one or more heteroatoms,
wherein the wetting agent and/or the surfactant (C2), decreases the surface tension of water below 68 mN·m−1 and wherein the wetting agent is selected from glycol compounds and having a molecular weight comprised between 60 g·mol−1 and 130 g·mol−1, and wherein the surfactant have a molecular weight comprised between 131 g·mol−1 and 300 g·mol−1.
wherein the step of mixing with water is carried out with a water to binder system (B) weight ratio comprised between 0.2 and 0.4.

31 more elements

A method for controlling mixability, rheology and/or open time of a wet concrete composition including aggregate (A), water (D) and a binder system (B), in an amount of 400 Kg per m3 of the wet concrete composition or less, comprising:

(B1) between 1% and 34% in dry weight of at least one lime source;
(B2) between 5% and 75% in dry weight of ground granulated blast furnace slag;
(B3) between 21% and 90% in dry weight of at least one filler,
(B4) between 0.1% and 5% in dry weight, relative to the total weight of components (B1), (B2), and (B3), of SO3;
said ground granulated blast furnace slag being a particles mixture of particles having a do greater than or equal to 5 μm and less than 15 μm, and optionally between 0.1% in weight, in respect with the total weight of the ground granulated blast furnace slag and 100% of particles having a do between 1 μm and less 5 μm.
said filler being a particles mixture of particles having a do greater than or equal to 0.05 μm and. less than 8 μm, and optionally between 0.1% and 50% in weight, in respect with the total weight of the filler of particles having a d50 greater than or equal to 8 μm and less than 200 μm,
measurement of d50 being done by Laser diffraction analysis by means of Laser diffraction analyzer with a humid way method,
wherein a water to binder system (B) weight ratio is comprised between 0.2 and 0.4,
said method including adding to said wet concrete composition an admixture formulation (C) comprises:
(C1) at least one water reducing polymer;
(C2) optionally a wetting agent and/or a surfactant;
said water reducing polymer (C1) being a polyethylene glycol bearing terminal phosphonate groups and/or a copolymer comprising the following monomeric units:
wherein:
represents a bonding site of a monomeric unit
the quantity of monomeric units UA is between 0 and 40 mol %,
the quantity of monomeric units UB is between 25 and 95 mol %,
the quantity of monomeric units UC is between 5 and 50 mol %,
the quantity of monomeric units UD is between 0 and 25 mol %,
R1 and R2 are independently hydrogen or methyl,
Z1 is a bond, a methyl or an ethyl,
Z2 is a bond, —CH2CH2O—, —CH2CH2OCH2CH2O— or —CH2CH2CH2CH2O—
R3 is —(CH2CH2O)m—R4, —(CH(CH3)CH2O)n—R4 or —(CH2CH2OCH(CH3)CH2O)y—R4,
m, n and y being an integer independently comprised between 7 and 100,
R4 is hydrogen, methyl,
R5 is hydrogen, methyl or —CH2COOH, and
R6 is —OH, —OCH2OH, —OCH2CH2OH, —OCH2CH2CH2OH, —OCH2CH(CH3)CH2OH, —OCH2CH2CH2CH2OH, —NHR7, a group bearing a phosphate function, a group bearing phosphonate function or a group bearing sulfonate function,
R7 being a saturated or unsaturated, linear or branched chain comprising from 2 to 12 carbon atoms and one or more heteroatoms,
wherein the wetting agent and/or the surfactant (C2), decreases the surface tension of water below 68 mN·m−1 and wherein the wetting agent is selected from glycol compounds and having a molecular weight comprised between 60 g·mol−1 and 130 g·mol−1, and wherein the surfactant have a molecular weight comprised between 131 g·mol−1 and 300 g·mol−.

25 more elements

A wet concrete composition comprising:

(A) at least one aggregate,
(B) a binder system, in an amount of 400 Kg per m3 of the wet concrete composition or less,
(C) an admixture formulation, and
(D) water,
wherein the binder system (B) comprises:
(B1) between 1% and 34% in dry weight of at least one lime source;
(B2) between 5% and 75% in dry weight of ground granulated blast furnace slag;
(B3) between 21% and 90% in dry weight of at least one filler,
(B4) between 0.1% and 5% in dry weight, relative to the total weight of components (B1), (B2), and (B3), of SO3;
said ground granulated blast furnace slag being a particles mixture of particles having a d50 greater than or equal to 5 μm and less than 15 μm, and optionally between 0.1% in weight, in respect with the total weight of the ground granulated blast furnace slag and 100% of particles having a d50 between 1 μm and less 5 μm.
said filler being a particles mixture of particles having a do greater than or equal to 0.05 μm and s less than 8 μm, and optionally between 0.1% and 50% in weight, in respect with the total weight of the filler of particles having a d50 greater than or equal to 8 μm and less than 200 μm,
measurement of d50 being done by Laser diffraction analysis by means of Laser diffraction analyzer with a humid way method,
wherein said admixture formulation (C) comprises:
(C1) at least one water reducing polymer;
(C2) optionally a wetting agent and/or a surfactant;
said water reducing polymer (C1) being a polyethylene glycol bearing terminal phosphonate groups and/or a copolymer comprising the following monomeric units:
wherein:
represents a bonding site of a monomeric unit
the quantity of monomeric units UA is between 0 and 40 mol %,
the quantity of monomeric units UB is between 25 and 95 mol %,
the quantity of monomeric units UC is between 5 and 50 mol %,
the quantity of monomeric units UD is between 0 and 25 mol %,
R1 and R2 are independently hydrogen or methyl,
Z1 is a bond, a methyl or an ethyl,
Z2 is a bond, —CH2CH2O—, —CH2CH2OCH2CH2O— or —CH2CH2CH2CH2O—
R3 is —(CH2CH2O)m—R4, —(CH(CH3)CH2O)n—R4 or —(CH2CH2OCH(CH3)CH2O)y—R4,
m, n and y being an integer independently comprised between 7 and 100,
R4 is hydrogen, methyl,
R5 is hydrogen, methyl or —CH2COOH, and
R6 is —OH, —OCH2OH, —OCH2CH2OH, —OCH2CH2CH2OH, —OCH2CH(CH3)CH2OH, —OCH2CH2CH2CH2OH, —NHR7, a group bearing a phosphate function, a group bearing phosphonate function or a group bearing sulfonate function,
R7 being a saturated or unsaturated, linear or branched chain comprising from 2 to 12 carbon atoms and one or more heteroatoms,
wherein the wetting agent and/or the surfactant (C2), decreases the surface tension of water below 68 mN·m−1 and wherein the wetting agent is selected from glycol compounds and having a molecular weight comprised between 60 g·mol−1 and 130 g·mol−1, and wherein the surfactant have a molecular weight comprised between 131 g·mol−1 and 300 g·mol−1, and
wherein a water to binder system (B.) weight ratio is comprised between 0.2 and 0.4.

30 more elements

Dependencies are inferred from the claim text.

Process for preparing wet concrete compositions and a method for controlling mixability, rheology and/or open time of wet concrete compositions

Life of this patent

Process for preparing wet concrete compositions and a method for controlling mixability, rheology and/or open time of wet concrete compositions

Life of this patent

Abstract

Claims10