Steel plate for pressure vessel with excellent cryogenic toughness and excellent ductility and manufacturing method thereof

A method of manufacturing a steel plate for a low temperature pressure vessel having excellent cryogenic toughness and ductility, the method comprising:

• reheating a steel slab at 1050 to 1250° C., the steel slab containing, in weight %, 0.05 to 0.15% of C, 0.20 to 0.40% of Si, 0.3 to 0.6% of Mn, 0.001 to 0.05% of Al, 0.012% or less of P, 0.015% or less of S, 4.0 to 5.0% of Ni, 0.001 to 0.10% of In, a balance of Fe, and unavoidable impurities;
• hot rolling the reheated steel plate at a reduction ratio of 5 to 30% per pass, and terminating rolling at a temperature of 800° C. or higher;
• primary cooling the hot-rolled steel plate at a cooling rate of 2.5 to 50° C./sec within 30 seconds after hot rolling;
• performing an intermediate heat treatment on the cooled steel plate for {2.4×t+(10−30)} minutes at a temperature of 690 to 760° C., where t is a thickness (mm) of a steel plate, and then, secondary cooling the steel plate at a cooling rate of 2.5 to 50° C./sec;
• and
• tempering the secondary cooled steel plate for {2.4×t+(10−30)} minutes at a temperature of 600 to 670° C., where t is a thickness (mm) of a steel plate.