Multilayer nanoporous separator
AssigneeLG Energy Solution, Ltd.
InventorsDavid W. Avison, Steven A. Carlson, Benjamin Sloan
Life of this patent
Estimating the term…
Abstract
A separator for a lithium battery having (a) a porous polymeric layer, such as a polyethylene layer; and (b) a nanoporous inorganic particle/polymer layer on both sides of the polymeric layer, the nanoporous layer having an inorganic oxide and one or more polymers; the volume fraction of the polymers in the nanoporous layer is about 15% to about 50%, and the crystallite size of the inorganic oxide is 5 nm to 90 nm.
Claims19
A separator for a lithium battery comprising:
- a porous polyethylene layer, and
- a second porous layer adjacent said porous polyethylene layer, said second porous layer comprises a first portion and second portion, wherein:
- the first portion is solid;
- and
- a. the first portion comprises boehmite particles and one or more polymers:
- b. a volume fraction of said one or more polymers in the first portion is between about 15% and about 50%;
- c. a total coating weight of said second porous layer on said porous polyethylene layer is about 5.5 grams per square meter or less, and
- d. a heat shrinkage of said separator at 150° C. for 1 hour is less than 5%.
5 more elements
A process for making a separator for a lithium battery comprising:
- (a) treating boehmite with an organic carbonate so as to make hydrophobic boehmite particles;
- (b) providing a porous polymeric layer;
- (c) providing a second porous layer, wherein said second porous layer comprises the hydrophobic boehmite particles and one or more polymers, and wherein the total coating weight of said second porous layer is less than 4.5 grams per square meter, and
- (d) bringing the second porous layer adjacent the porous polymeric layer, so as to make a separator with no more than 600 parts per million of water.
1 more element
A device comprising:
- a porous polyethylene layer, and
- a second porous layer adjacent said porous polyethylene layer, said second porous layer comprises a first portion and second portion, wherein:
- the first portion is solid;
- and
- a. the first portion comprises boehmite particles have an average crystallite size between 5 nm and 90 nm and one or more polymers:
- b. a volume fraction of said one or more polymers in the first portion is between about 25% and about 40%;
- c. a total coating weight of said second porous layer on said porous polyethylene layer is about 5.5 grams per square meter or less, and
- d. a heat shrinkage of said separator at 150° ° C. for 1 hour is less than 5%.
5 more elements