The present invention relates to the manufacturing a wood-polymer composite. It is directed to a method for manufacturing such a composite, including the provision of a wood element (1), the impregnation of the wood element with a lactic acid water-based solution (2), and then the thermal treatment of the impregnated wood element (3) at a heating temperature higher than a nominal temperature where the in-situ polymerization of the lactic acid is initiated, in order both to induce the diffusion of the lactic water-based solution acid water-based solution within the impregnated wood element and to initiate the in-situ polymerization of the lactic acid. According to the invention, the thermal treatment (3) includes the acceleration of the increase of the heating temperature and/or the decreasing of the nominal temperature.
A method for manufacturing a wood-polymer composite, including the provision of a wood element (1), the impregnation of the wood element with a lactic acid water-based solution (2), and then the thermal treatment of the impregnated wood element (3) at a heating temperature (T) higher than a nominal temperature where the in-situ polymerization of the lactic acid is initiated (T0), in order both to induce the diffusion of the lactic acid water-based solution within the impregnated wood element and to initiate the in-situ polymerization of the lactic acid, characterized in that the thermal treatment (3) includes the acceleration of the increase of the heating temperature (T) and/or the decreasing of the nominal temperature (T0).
The method according to any of claims 2 to 4, wherein the thermal treatment by microwaves radiations takes place during 2 to 72 hours, at a temperature between 140 to 180° C.
The method according to any of the preceding claims, wherein the decreasing of the nominal temperature (T0) is achieved by a thermal treatment under vacuum conditions.
The method according to any of the preceding claims, wherein after the wood element is impregnated and before it is thermally treated, the impregnated wood element is pre-heated (4) so as to increase its temperature and then to reduce the time need for the impregnated wood element to reach the polymerization temperature during the thermal treatment.
The method according to any of the preceding claims, wherein after the wood element is impregnated and before it is thermally treated, the impregnated wood element is vacuum pre-dried (4) so as to reduce the water content of the impregnated wood element and then to reduce the amount of energy necessary to evaporate water before the polymerization starts.
The method according to any of the preceding claims, wherein the impregnation (2) with an lactic acid water-based solution is made under vacuum.
The method according to any of the preceding claims, wherein the lactic acid water-based solution includes more than 70% of lactic acid.
A wood-polymer composite obtainable by implementing the method according to any of the preceding claims.