A polymer composition comprising:

• 100 parts by weight of a polymer matrix that includes at least one polyarylene sulfide in an amount of from about 10 wt. % to about 60 wt. % of the polymer composition and at least one condensation polymer in an amount of from about 5 wt. % to about 35 wt. % of the polymer composition;
• from about 1 to about 30 parts by weight of at least one laser activatable additive;
• from about 40 to about 100 parts by weight of inorganic fibers;
• and
• wherein the polymer composition exhibits a dielectric constant of about 5 or less at a frequency of 2 GHz, a flexural modulus of about 13,500 MPa or more as determined at a temperature of 23° C. in accordance with ISO 178:2019, and a deflection temperature under load of about 260° C. or more as determined in accordance with ISO 75:2013 at a load of 1.8 MPa.