Grain-oriented electrical steel sheet, method for manufacturing grain-oriented electrical steel sheet, and method for evaluating grain-oriented electrical steel sheet

A method of producing a grain oriented electrical steel sheet comprising forming a coating on each of both surfaces of a steel sheet by applying a coating liquid to the steel sheet, followed by baking at a temperature of not lower than 700° C., and cooling, while the steel sheet is transported,

• wherein a forward slip r in a transport region in which the steel sheet is cooled to a temperature of not higher than 600° C. is not more than 1.7%, and
• wherein in the coating liquid,
• a molar ratio M1/S of a content of a metal element M1 to a content of a silica S in terms of SiO2 is not less than 0.15,
• a molar ratio M2/S of a content of a metal element M2 to the content of the silica S in terms of SiO2 is not more than 0.15, and
• a molar ratio P/S of a content of a phosphoric acid component P in terms of P2O5 to the content of the silica S in terms of SiO2 is not less than 0.20,
• the metal element M1 being at least one selected from the group consisting of Zn, Li, Mg, and Ca, and the metal element M2 being at least one selected from the group consisting of Zr, Ti, Cr, and Al.

A method of evaluating a grain oriented electrical steel sheet comprising:

• a steel sheet;
• and a coating provided on each of both surfaces of the steel sheet, the method comprising
• conducting a rubbing test to obtain an interlaminar current value of the grain oriented electrical steel sheet after the rubbing test, and determining whether insulation property of the grain oriented electrical steel sheet is good or not based on the interlaminar current value obtained,
• the rubbing test being conducted by stacking two sheets of the grain oriented electrical steel sheet and rubbing the two sheets against each other to make 60 to 120 reciprocations under conditions of a surface pressure of 150 to 250 Pa, a rubbing speed of to 0.15 m/s, and a reciprocating stroke of 30 to 70 mm.