Crystalline boehmite materials as precursors for large crystal gamma alumina and low surface area alpha alumina
AssigneeBASF SE
InventorsKarl C. Kharas, Danna Mooney
Life of this patent
Estimating the term…
Abstract
A process for preparing crystalline boehmite includes combining a stoichiometric amount of flash calcined gibbsite (AI2O3) and gibbsite (Al(OH)3) in a pressurizable reaction vessel; heating the flash calcined gibbsite and gibbsite in the reaction vessel to a temperature of about 200° C. to about 280° C. and for a time sufficient to form crystalline boehmite. A crystalline boehmite exhibiting a crystallite from about 600 Å to about 850 Å when measured in the 120 direction of the crystallographic space group Cmcm.
Claims30
A crystalline boehmite exhibiting a crystallite from about 600 Å to about 850 Å when measured in the 120 direction of the crystallographic space Cmcm.
A process for preparing crystalline boehmite, the process comprising:
- combining a stoichiometric amount of flash calcined gibbsite (Al2O3) and gibbsite (Al(OH)3) in a pressurizable reaction vessel;
- heating the flash calcined gibbsite and gibbsite in the reaction vessel to a temperature of about 200° C. to about 280° C. and for a time sufficient to form crystalline boehmite.
(canceled)
(canceled)
A process for preparing a transitional alumina, the process comprising:
- preparing crystalline boehmite via a stoichiometric process comprising:
- combining stoichiometric amounts of flash calcined gibbsite (Al2O3) and gibbsite (Al(OH)3) in a pressurizable reaction vessel;
- heating the flash calcined gibbsite and gibbsite in the reaction vessel to a temperature of about 200° C. to about 280° C. and for a time sufficient to form crystalline boehmite;
- and
- calcining the crystalline boehmite to form the transitional alumina.
(canceled)
(canceled)
(canceled)
(canceled)
(canceled)
(canceled)
A FCC catalyst comprising Y-zeolite and a crystalline boehmite comprising a crystallite size of about 600 Å to about 850 Å.
(canceled)
(canceled)