Pressure-sensitive adhesive sheet and use thereof
AssigneeNitto Denko Corporation
InventorsYosuke SHIMIZU, Naofumi KOSAKA, Ryoko ASAI, Kenta KUMAKURA
Life of this patent
Estimating the term…
Abstract
Provided is a PSA sheet that can combine bonding reliability and peeling removability, and further can be peeled off without causing deformation or damage to the adherend in various peeling modes. The PSA sheet provided by this invention has a PSA layer. The PSA sheet has a water-peel strength of 2 N/10 mm or less. The PSA sheet further has a stress at 100 % elongation of less than 30 MPa as well as a multiplication product (σf-εf) of fracture stress σf (MPa) and fracture strain εf (%) of 250 or greater.
Claims12
A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer, the pressure-sensitive adhesive sheet having a water-peel strength of 2 N/10 mm or less, determined after the adhesive face of the pressure-sensitive adhesive layer is applied to the surface of an alkaline float glass plate adherend having a contact angle of 5° to 10° with distilled water, the resultant is stored at room temperature for one day, 20 µL of distilled water is dropped onto the adherend and the distilled water is allowed to enter an interfacial edge between the adhesive face and the adherend;
- according to JIS Z0237:2009 “10.4.1 Method 1:
- 180° Peel Strength to Test Plate”;
- specifically, at a test temperature of 23° C. at a tensile speed of 300 mm/min at a peel angle of 180° using a tensile tester;
- and
- further having a stress at 100 % elongation of less than 30 MPa as well as a multiplication product (σf•εf) of fracture stress σf (MPa) and fracture strain εf (%) of 250 or greater, wherein the stress at 100 % elongation, the fracture stress σf and the fracture strain εf are determined based on a tensile test carried out at a tensile speed of 100 mm/min.
A pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer, wherein
- the pressure-sensitive adhesive layer comprises at least one species of compound selected among surfactants and polyoxyalkylene backbone-containing compounds, and
- the pressure-sensitive adhesive sheet has a stress at 100 % elongation of less than 30 MPa and as well as a multiplication product (σf•εf) of fracture stress σf (MPa) and fracture strain εf (%) of 250 or greater, wherein the stress at 100 % elongation, the fracture stress σf and the fracture strain εf are determined based on a tensile test carried out at a tensile speed of 100 mm/min.
A method for peeling a stretchable pressure-sensitive adhesive sheet adhered on an adherend, the method comprising
- a step of pulling and peeling the pressure-sensitive adhesive sheet in a < 90° direction relative to the bonding interface with the adherend, wherein
- the pressure-sensitive adhesive sheet peeling step is carried out in the presence of aqueous liquid where subjected to peeling in the bonding interface between the adherend and the pressure-sensitive adhesive sheet.
A method for separating two adherends joined with a stretchable pressure-sensitive adhesive sheet, the method comprising
- a step of pulling the pressure-sensitive adhesive sheet in a direction to pull it out from between the two adherends, wherein
- the pressure-sensitive adhesive sheet pulling step is carried out in the presence of aqueous liquid where subjected to peeling in the bonding interface between the pressure-sensitive adhesive sheet and at least one of the two adherends.
Dependencies are inferred from the claim text.