Thermosetting resin composition, thermosetting resin cured product, prepreg and fiber-reinforced composite material

Abstract

A thermosetting resin composition contains at least: [A] a thermosetting resin; [B] a curing agent; and [C] polyamide particles satisfying following (c1) to (c6): (c1) a melting point of polyamide resin constituting the polyamide particles is 200 to 300° C.; (c2) a crystallization temperature of the polyamide resin constituting the polyamide particles is 150° C. to 250° C.; (c3) a number average particle size of the polyamide particles is 1 to 100 μm; (c4) a sphericity of the polyamide particles is 80 to 100; and (c5) the linseed oil absorption of the polyamide particles is 10 to 100 mL/100 g. A thermosetting resin composition of the present invention enables suitable production of a fiber-reinforced composite material having sufficient compressive strength after impact and wet heat compression performance.