Non-grain oriented electrical steel and method for manufacturing same

A manufacturing method of a non-oriented electrical steel sheet, comprising:

• heating a slab that includes, in wt %, C at 0.004 wt % or less (excluding 0 wt %), Si at 2.5 to 4.0 wt %, P at 0.1 wt % or less (excluding 0 wt %), Al at 0.3 to 2.0 wt %, N at 0.003 wt % or less (excluding 0 wt %), S at 0.003 wt % or less (excluding 0 wt %), Mn at 0.15 to 2.5 wt %, Cr at 0.5 wt % (excluding 0 wt %), and the balance including Fe and other impurities unavoidably added thereto and that satisfies Equation 1 below;
• hot-rolling the slab to manufacture a hot rolled sheet;
• cold rolling the hot rolled sheet to manufacture a cold rolled sheet;
• and
• final annealing the cold rolled sheet at a temperature of 710 to 820° C.
• [Mn]≥1450×[S]−0.8 [Equation 1]
• (in Equation 1, [Mn] and [S] represent a content (wt %) of Mn and S, respectively.)