Surface modification method for fluoride luminescent material and fluoride luminescent material prepared therefrom

Abstract

In a surface modification method for fluoride luminescent materials, an inorganic coating layer AxMFy coated substrate AxMFy:Mn4+ is mixed with an organic solution containing a metal phosphate, an alkoxysilane, an organic carboxylic acid or an organic amine. The solution is evaporated to give the organic-inorganic coating layer coated surface-modified fluoride luminescent material. The phosphor photoluminescence intensity and quantum efficiency of the modified phosphors can be maintained at 85%-95% under high temperature and high humidity conditions. After being coated with the inorganic coating layer, the surface defects of the phosphor are reduced, and the photoluminescence intensity and quantum yield of the phosphor are increased by 5%-15%. After being coated with the organic coating layer, the photoluminescence intensity of the phosphor is reduced <3%.