Composition of matter for inhibiting water migration between inside and outside of concrete

A composition of matter, comprising a phlogopite powder or muscovite powder, clinoptilolite or mordenite, and kaolinite, and the composition of matter being prepared as follows:

• 1) grinding the phlogopite powder or muscovite powder and sieving using a 300-400 mesh sieve, and drying;
• grinding the clinoptilolite or mordenite and sieving using a 300-mesh sieve;
• and calcining the kaolinite at a temperature of 750-800° C., and grinding the kaolinite calcined and sieving using a 500-mesh sieve;
• 2) mixing the phlogopite powder or muscovite powder, the clinoptilolite or mordenite, and the kaolinite in a weight ratio of 50-70:0-30:0-50;
• adding a solution comprising isopropanol and n-butanol to a mixture of the phlogopite powder or muscovite powder, the clinoptilolite or mordenite, and the kaolinite, thereby yielding a mixed solution;
• ultrasonically treating the mixed solution for 10 min, and then magnetically stirring the mixed solution for 10 min at a first rotational speed;
• 3) adding a silane coupling agent to the mixed solution, and continuously magnetically stirring the mixed solution mixed with the silane coupling agent for 30 min;
• adding distilled water to the mixed solution mixed with the silane coupling agent, and continuously magnetically stirring for 30 min at a second rotational speed greater than the first rotational speed;
• and adding methyl silicone oil to the mixed solution mixed with the silane coupling agent and the distilled water, and magnetically stirring for an hour, thereby yielding a slurry;
• and
• 4) drying the slurry at a temperature of 150-200° C. into powders, and grinding and sieving the powders, thereby yielding the composition of matter.