Method of producing concentrated or dried acid-gellable whey protein aggregates, and related compositions and food products
AssigneeArla Foods Amba
InventorsMette Møller Andersen, Søren Bang Nielsen, Hans Bertelsen
Life of this patent
Estimating the term…
Abstract
The present invention relates to a novel method for preparing acid-gellable whey protein aggregates in the form of concentrated suspensions or powders. Moreover, the present invention relates to a novel composition containing the acid-gellable whey protein aggregates, to a food product ingredient comprising the novel type of acid-gellable whey protein composition, and to a food product comprising the novel type of acid-gellable whey protein composition.
Claims25
A method of preparing an acid-gellable whey protein composition said method comprising the steps of:
- a) providing a demineralised solution comprising 1-15% (w/w) native, denaturable whey protein and having a pH in the range of 6-9,
- b) heat-treating the demineralised solution of step a) to a temperature of at least 68 degrees C. for at most 2 hours, thereby obtaining a suspension comprising acid-gellable whey protein aggregates,
- c) cooling the suspension of step b) to a temperature of at most 30 degrees C.,
- d) concentrating the suspension obtained in step c) to a concentration of acid-gellable whey protein aggregates of at least 4% (w/w),
- e) drying the concentrated suspension,
- wherein:
- the temperature of the concentrated suspension of step d) is maintained at at most 30 degrees C. until the concentrated suspension is subjected to the drying of step e), and
- the duration between the concentration of step d) and the drying of step e) is at most 48 hours.
The method according to any of the preceding claims, wherein the demineralised solution comprises 3-15% (w/w) native, denaturable whey protein.
The method according to any of the preceding claims, wherein the demineralised solution has a pH in the range of 6-8.
The method according to any of the preceding claims, wherein the suspension is concentrated until a concentration of acid-gellable whey protein aggregates of at least 6% (w/w) is obtained.
The method according to any of the preceding claims, wherein the concentrated suspension obtained in step d) is produced by subjecting the suspension to ultrafiltration, nano-filtration and/or reverse osmosis.
The method according to any of the preceding claims, wherein the cooled suspension of step c) is mixed with native whey protein before concentrating the suspension in step d) or the concentrated suspension of step d) is mixed with native whey protein before drying the concentrated suspension in step e).
The method according to any of the preceding claims, wherein the total amount of combined calcium and magnesium in the demineralised solution of step a) is at most 120 mmol/kg dry weight.
The method according to any of the preceding claims, wherein the temperature of the concentrated suspension of step d) is maintained at at most 20 degrees C. until the concentrated suspension is either subjected to the drying of step e).
The method according to any of the preceding claims, wherein the acid-gellable whey protein composition is a dry powder.
A method of preparing a food product said method comprising the steps of:
- a) providing a demineralised solution comprising 1-15% (w/w) native, denaturable whey protein and having a pH in the range of 6-9,
- b) heat-treating the demineralised solution of step a) to a temperature of at least 68 degrees C. for at most 2 hours, thereby obtaining a suspension comprising acid-gellable whey protein aggregates,
- c) cooling the suspension of step b) to a temperature of at most 30 degrees C.,
- d) concentrating the suspension obtained in step c) to a concentration of acid-gellable whey protein aggregates of at least 4% (w/w), and
- subsequently using the concentrated suspension of acid-gellable whey protein aggregates of step d) as an ingredient in the production of the food product,
- wherein:
- the temperature of the concentrated suspension of step d) is maintained at at most 30 degrees C. until the subsequent use of the concentrated suspension, and
- the duration between the concentration of step d) and the subsequent use of the concentrated suspension is at most 48 hours.