Glue Grease and method of making
OwnerMahdi Hosseiniinventor
Life of this patent
Estimating the term…
Abstract
Glue Grease, has been designed and made as a lubricant to be used in moving mechanical parts in difficult environmental conditions as an anti-abrasion material in order to increase the longevity of parts prone to friction.
Claims8
1- A method for making glue grease, comprising
- In a first mixer, a predetermined quantity of Latex and Ammonia are mixed till a homogenous white solution is created;
- then in a second mixer that is a kept at a predetermined temperature a second quantity of Mazut oil is mixed with a portion of said white solution;
- creating a second solution.
2- The method of claim 1, wherein said Mazut oil is composed of Alkane hydrocarbon chains containing from 20 to70 carbon atoms in each chain;
- and wherein said Mazut oil is low-Sulphur Mazut oil, with a Sulphur content of 1.0-1.5%.
3- The method of claim 2, wherein said Latex is an adhesive polymer acquired both from natural sources (plant saps) and synthetically through polymerization of isoprene;
- wherein either form is suitable.
4- The method of claim 3, wherein said second mixer is turned on for 3 hours, wherein vulcanization process happens between said Latex and said Sulphur content of said Mazut oil.
5- The method of claim 4, wherein in said 3 hours, said Latex is oxidized and said Sulphur turns into Sulphide, therefore a third solution with elasticity and anti-abrasion characteristic is created.
6- The method of claim 5, wherein after said 3 hours said second mixer is turned off and said third solution is let to rest for at least 12 hours, creating a paste like black polymer that is oily and elastic (glue grease).
7- The method of claim 6, wherein said predetermined quantity is 400 grams of said Latex and 700 grams of said 44% Ammonia, and wherein said portion of said white solution is 300 ml, and wherein said second quantity is 1 liter of said low-Sulphur Mazut oil.
8- The method of claim 7, wherein said final glue grease solution comprises a lot of capabilities but not limited to being anti-abrasion and lubricant;
- having high viscosity and elasticity;
- being resistance to temperatures as high as 450 degrees centigrade;
- and resistance to temperatures as low as −90 degrees centigrade.