Tire with rubber tread containing a combination of styrene/butadiene elastomers and traction resins and pre-hydrophobated precipitated silica reinforcement

A pneumatic tire is provided having an outer circumferential tread with a tread running surface where said tread is a rubber composition comprised of, based on parts by weight per 100 parts by weight rubber (phr),

• (A) conjugated diene-based elastomers comprised of:
• (1) about 20 to about 70 phr of a solution polymerization prepared styrene/butadiene elastomer (S-SBR-A) having a styrene content in a range of from about 35 to about 45 percent and a Tg in a range of from about −30° C. to about −50° C.,
• (2) about 20 to about 60 phr of a solution polymerization prepared styrene/butadiene elastomer (S-SBR-B) having a styrene content in a range of from about 35 to about 45 percent and a Tg in a range of from about −3° C. to about −23° C., and
• (3) about 5 to about 30 phr of an aqueous emulsion polymerization prepared styrene/butadiene elastomer (E-SBR) having a styrene content in a range of from about 35 to about 45 percent and a Tg in a range of from about −30° C. to about −50° C., wherein said Tg's of said S-SBR-A, S-SBR-B and E-SBR are spaced apart from each other by at least about 4° C.;
• (B) about 8 to about 30 phr of from about 3 to about 5 traction promoting resins individually present in a range of from about 0.5 to about 15 phr, selected from:
• (1) polyester phthalate resin, having a softening point in a range of from about 20° C. to about 26° C.,
• (2) styrene/alphamethyl styrene resin, having a softening point in a range of from about 80° C. to about 90° C.,
• (3) gum rosin, having a softening point in a range of from about 70° C. to about 100° C., desirably about 80° C. to about 90° C.,
• (4) coumarone indene resin, having a softening point in a range of from about 90° C. to about 120° C., and alternately
• (5) alkylphenol acetylene resin having a softening point in a range of from about 130° C. to about 150° C.;
• (C) about 50 to about 130 phr of rubber reinforcing filler comprised of rubber reinforcing carbon black and pre-hydrophobated precipitated silica containing from about 40 to about 100 phr of said rubber reinforcing carbon back, wherein the weight ratio of said rubber reinforcing carbon black to said precipitated silica is at least about 70/30, wherein said pre-hydrophobated precipitated silica is a precipitated silica treated with at least one of alkoxyorganomercaptosilane and bis(3-trialkoxysilylorgano) polysulfide containing an average of from about 2 to about 4 connecting sulfur atoms in its polysulfidic bridge.