Porous stamp material for laser processing, porous stamp using the same, and method of manufacturing the same

Abstract

The invention provides a porous stamp material for laser processing that is available for continuous extrusion molding. A material including at least 100 parts by weight of thermoplastic resin, 50-250 parts by weight of hydroxylated compound whose dehydration starting temperature is 100 to 500° C., and water-soluble pore-forming material that has 10-60 μm average particle diameter is mixed to obtain a mixed material. The obtained mixed material is extruded to obtain an extrusion molded product. The obtained extrusion molded product is processed with an aqueous solvent to elute the water-soluble pore-forming material, thereby yielding a porous stamp material that has continuous pores having 10-60 μm pore diameter. The obtained porous stamp material is laser-processed to manufacture a stamp.