Back to results
US 2016/0260602 A1Published application
Adhesion improvements for oxide-silicon stack
AssigneeApplied Materials, Inc.
InventorsSubbalakshmi SREEKALA, Nagarajan RAJAGOPALAN, Bok Hoen KIM
Life of this patent
Estimating the term…
Abstract
Embodiments generally relate to methods of controlling hydrogen content in a silicon oxide/amorphous silicon stack. By precleaning the substrate of residues, controlling the delivery of hydrogen during the stack deposition and preventing outgassing of hydrogen from deposited layers during subsequent layer deposition and processing, the effects of delamination can be avoided in the formation of devices, such as 3D NAND devices.
Claims20
A method comprising:
- positioning a substrate in a processing chamber;
- energizing a preclean gas into a plasma to create an energized preclean gas;
- delivering the energized preclean gas to the substrate;
- purging the processing chamber;
- and
- depositing one or more silicon oxide/silicon containing stacks on a substrate in the presence of a vacuum, wherein depositing a silicon oxide/silicon-containing stack comprises:
- energizing a first process gas into a first plasma;
- depositing a first material layer on the substrate from the first plasma;
- energizing a second process gas into a second plasma;
- depositing a layer of a second material on the substrate from the second plasma;
- and
- repeating the above steps until a predetermined number of the first material layers and the second material layers have been deposited on the substrate, wherein the first material layer and the second material layer are either a silicon oxide layer or an amorphous silicon layer and wherein the second material layer is different from the first material layer.
9 more elements
A method of forming a stack comprising:
- energizing a first process gas into a first plasma;
- depositing a first material layer on the substrate from the first plasma, the layer of the first material having a first thickness;
- plasma purging the PECVD chamber to expose a surface of the first material layer, creating first gas contaminants;
- gas purging the PECVD chamber to remove the first gas contaminants;
- energizing a second process gas into a second plasma;
- depositing a second material layer on the first material layer from the second plasma, the second material layer having a second thickness;
- plasma purging the PECVD chamber to expose a surface of the second material layer, creating second gas contaminants;
- gas purging the PECVD chamber to remove the second gas contaminants;
- and
- repeating the above steps until a predetermined number of the first material layers and the second material layers have been deposited on the substrate, wherein, during at least one of the above steps, at least a portion of the chamber, the substrate support or combinations thereof is maintained at a temperature of between about 500 degrees Celsius and about 650 degrees Celsius, wherein the first material layer and the second material layer are either a silicon oxide layer or an amorphous silicon layer and wherein the second material layer is different from the first material layer.
7 more elements
A method of forming a stack comprising:
- energizing a first process gas into a first plasma;
- depositing a first material layer on the substrate from the first plasma, the layer of the first material having a first thickness, the substrate being maintained at a temperature between 500 degrees Celsius and 650 degrees Celsius;
- plasma purging the PECVD chamber to expose a surface of the first material layer, creating first gas contaminants;
- gas purging the PECVD chamber to remove the first gas contaminants;
- energizing a second process gas into a second plasma;
- depositing a second material layer on the first material layer from the second plasma, the second material layer having a second thickness, the substrate being maintained at a temperature between 500 degrees Celsius and 650 degrees Celsius, wherein the first material layer has a first thickness and the second material layer has a second thickness, and wherein the first thickness is less than the second thickness;
- plasma purging the PECVD chamber to expose a surface of the second material layer, creating second gas contaminants;
- gas purging the PECVD chamber to remove the second gas contaminants;
- and
- repeating the above steps until a predetermined number of the first material layers and the second material layers have been deposited on the substrate, wherein, during at least one of the above steps, at least a portion of the chamber, the substrate support or combinations thereof is maintained at a temperature of between about 500 degrees Celsius and about 650 degrees Celsius, wherein the first material layer and the second material layer are either a silicon oxide layer or an amorphous silicon layer and wherein the second material layer is different from the first material layer.
7 more elements
Dependencies are inferred from the claim text.