Thin film formation method, thin film, and glass plate having thin film attached thereto

Abstract

The present invention relates to a method for forming a TiO2 thin film on a substrate by using an atmospheric pressure CVD method, in which a raw material gas contains titanium tetraisopropoxide (TTIP) and a chloride of a metal M vaporizable in a temperature range of 100 to 400° C. and the amount of the chloride of the metal M is from 0.01 to 0.18 as a concentration ratio to the titanium tetraisopropoxide (TTIP) (chloride of metal M (mol %)/TTIP (mol %)).