AssigneeIntermet Technologies Chengdu Co., Ltd.
InventorsLin Gao, Tao Wang, Bo Li
Estimating the term…
Disclosed are a powder sintered porous metal with better comprehensive properties, especially with good corrosion resistance to hydrofluoric acid, and a filter element using same. The powder sintered porous metal of the present invention has a porosity of 25-60%, an average pore diameter of 0.5-50 μm and a weight loss rate of at most 1% after being immersed into a hydrofluoric acid solution with a mass fraction of 5% at room temperature for 20 days; and the powder sintered metal porous body consists of Cu accounting for 23-40 wt %, Si accounting for 0-5% and the balance of Ni, based on the weight of the powder sintered metal porous body. The powder sintered porous metal of the present invention has good mechanical properties and machinability, and excellent corrosion resistance in acid mediums, especially in hydrofluoric acid mediums. In particular surprisingly, when Cu and Ni are introduced into the powder sintered porous metal by Cu element powders and Ni element powders doped in the raw material powders, the powder sintered porous metal has significantly improved permeability and backflushing regeneration property.
A powder sintered porous metal with a porosity of 25-60% and an average pore diameter of 0.5-50 μm is characterized in that, the powder sintered metal porous body consists of 23-40 wt % of Cu, 0-5 wt % of Si and the balance of Ni, and has a weight loss rate of at most 1% after being immersed into a hydrofluoric acid solution with a mass fraction of 5% at room temperature for 20 days.
A method for improving the permeability of the powder sintered porous metal, the powder sintered porous metal has a porosity of 25-60% and an average pore diameter of 0.5-50 μm, and consists of 23-40 wt % of Cu, 0-5 wt % of Si and the balance of Ni;
Dependencies are inferred from the claim text.