Booster antenna and method for producing same

Abstract

A silver particle dispersing solution, which contains 50-70% by weight of silver particles having an average particle diameter of 20 nm or less, is applied on a substrate by the flexographic printing, and then, calcined to produce a booster antenna wherein a silver conductive film, which contains 10-50% by volume of a sintered body of the silver particles and which has a volume resistivity of 3-100 μΩ·cm, a surface resistivity of 0.5Ω/□ or less and a thickness of 1-6 μm, is formed on the substrate. Thus, there is provided a booster antenna which has excellent electrical characteristics and flexibility and which can be inexpensively mass-produced.