Pin hole evaluation method of dielectric films for metal oxide semiconductor tft
AssigneeApplied Materials, Inc.
InventorsDong-Kil YIM, Tae Kyung WON, Seon-Mee CHO
Life of this patent
Estimating the term…
Abstract
The present invention generally relates to methods measuring pinhole determination. In one aspect, a method of measuring pinholes in a stack, such as a TFT stack, is provided. The method can include forming an active layer on a deposition surface of a substrate, forming a dielectric layer over the active layer, delivering an etchant to at least the dielectric layer, to etch both the dielectric layer and any pinholes formed therein and optically measuring the pinhole density of the etched dielectric layer using the active layer.
Claims20
A method of analyzing a device, comprising:
- forming an active layer on a deposition surface of a substrate;
- forming a dielectric layer over the active layer;
- etching at least the dielectric layer to remove at least 40 percent of the dielectric layer creating an etched dielectric layer;
- and
- optically measuring a pinhole density of the etched dielectric layer using the active layer.
A method of detecting pinholes, sequentially comprising:
- positioning a substrate in a processing chamber, the substrate comprising:
- an active layer;
- and
- a dielectric layer having a thickness;
- delivering a halogen-containing etchant to the dielectric layer to etch the thickness of the dielectric layer to be approximately equal to the thickness of the active layer, wherein portions of the active layer are exposed by the halogen containing etchant;
- etching the exposed portions of the active layer creating one or more void regions;
- and
- examining the substrate for void regions in the active layer, each of the void regions corresponding to a pinhole in the dielectric layer.
A method of analyzing a device, comprising:
- positioning a substrate in a processing chamber, the substrate having a deposition surface;
- forming an IGZO active layer on the deposition surface, the IGZO layer deposited to a first thickness;
- forming a silicon oxide layer over the IGZO active layer to a second thickness;
- delivering an etchant comprising HF to the silicon oxide layer, the etchant removing approximately 50% of the second thickness of the silicon oxide layer, wherein portions of the IGZO active layer are exposed to the etchant;
- etching the exposed portions of the IGZO active layer creating one or more void regions;
- and
- examine the substrate for void regions formed by the etchant in the IGZO active layer, each of the void regions corresponding to a pinhole in the silicon oxide layer.