High strength tape articles from ultra-high molecular weight polyethylene

Abstract

Tape articles having improved properties are made from ultra-high molecular weight (UHMW) multi-filament yarns. The tape articles can have a ratio of the low temperature area under the curve (120° C. to Tm-onset) to the total area under the curve (120° C. to 165° C.) of less than about 0.15 as calculated from an increasing temperature DSC scan from a temperature of 30° C. to a temperature of 200° C. at a constant rate of 10° C. per minute. Additionally, in some examples the tape articles can also have a tenacity at least about 24 g/d (2.06 GPa) when measured by ASTM D882-09 at a 10 inch (25.4 cm) gauge length and at an extension rate of 100%/min. Further, the tape articles can have no long period of less than 450 Angstroms (Å) when measured by small angle x-ray analysis.