US 2014/0154520 A1Published application
Embossed Metallic Flakes Process And Product
AssigneeEckart America Corporation
InventorJames P. Rettker
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeEckart America Corporation
InventorJames P. Rettker
Estimating the term…
A process for preparing embossed fine particulate thin metal flakes having high levels of brightness and color intensity. The process comprises forming a release coat on a flexible polymeric carrier film, embossing the release coat with a diffraction grating pattern that is monoruled at an angle above 45°, vacuum metalizing the embossed release surface with a highly reflective metal such as aluminum, and solubilizing the metalized release coat in a solvent for removing the metal from the carrier to form embossed metal flakes that replicate the embossment pattern. The flakes are recovered from the solution containing the solvent and release coat polymer while avoiding high shear, particle sizing or other application of energy that would excessively break up the flakes, so that the D50 particle size of the flakes is maintained at or above 75 microns. The flakes have application to coatings and printing inks that produce extremely high brightness characterized as an optically apparent glitter or sparkle effect in combination with high color intensity or chromaticity.
1-21. (canceled)
Reflective metal flakes which have been embossed by replicating a diffraction grating pattern having a monoruled embossing angle above 45°, the embossed flakes having a D50 average particle size at or above 75 microns, and a flake thickness from about 50 mu to about 100 nm.
The reflective metal flakes of claim 21 in which the diffraction grating pattern has from about 5,000 to less than about 14,000 grooves per cm.
The product of claim 21 in which the embossed flakes have a groove depth to flake thickness ratio of greater than 1.0.
A product comprising a dry film coating, wherein the embossed flakes of claim 21 are contained in said dry film coating and said dry film coating has a greater measured chromaticity and color intensity at 75° and 110° (measured via a multi-angle spectrophotometer) when compared with a coating containing flakes embossed at a diffraction grating pattern at 45° and having a particle size of 50 microns.
A printing ink containing the embossed flakes of claim 21.
A multi-layer laminate having a decorative layer with a print pattern made from a coating or printing ink containing the embossed flakes of claim 21.
A resinous coating containing the embossed flakes of claim 21 that produce increased reflectivity across all colors of the color spectrum.
The embossed flakes of claim 21 in which the embossed flakes have an optical density of 3.0 or more and a D50 average flake size greater than 200 microns.
Reflective metal flakes which have been embossed by replicating a diffraction grating pattern having a monoruled embossing angle above 45°, the embossed flakes having a D50 average particle size at or above 75 microns, and a flake thickness from about 50 nm to about 100 nm, a diffraction grating pattern of less than about 14,000 grooves per centimeter, and a groove depth of less than about 140 nm.
Reflective metal flakes which have been embossed by replicating a diffraction grating pattern having a monoruled embossing angle at about 60°, the embossed flakes having a D50 average particle size at or above 75 microns, and a flake thickness from about 50 nm to about 100 nm.