Aluminum Coated Steel Sheet Having Excellent Oxidation Resistance and Heat Resistance

Abstract

Provided is an aluminum coated steel sheet having excellent oxidation and heat resistance. The aluminum coated steel sheet includes an aluminum coating layer and an alloy layer. The aluminum coating layer is formed on a surface of a steel sheet which includes 0.001 to 0.015 wt % of carbon (C), 0.05 to 0.3 wt % of silicon (Si), 0.1 to 0.6 wt % of manganese (Mn), 0.01 to 0.05 wt % niobium (Nb), 0.01 wt % or less of phosphorus (P), 0.01 wt % or less of sulfur (S), 0.1 wt % or less of soluble aluminum (Al), 0.05 to 0.5 wt % of copper (Cu), 0.05 to 0.5 wt % nickel (Ni), 0.001 to 0.01 wt % of nitrogen (N), and the balance of Fe and inevitable impurities. The alloy layer includes an intermetallic compound at an interface between the steel sheet and the aluminum coating layer.