Expandable Graphite Particles and Methods of Making Same
AssigneeW. L. Gore & Associates, Inc.
InventorsMukesh Jain, Dattatreya Panse
Life of this patent
Estimating the term…
Abstract
Small particle size expandable graphite materials are described which are highly expandable, as well as methods of making such unique graphite materials. In one embodiment, expandable graphite particles are described having a particle size nominally between about 100 and 200 US mesh, a chromium content of less than 5 parts per million (ppm) and an expansion of about 80 cc/g or greater when heated at about 500° C.
Claims10
A method of making expandable graphite particles, said expandable graphite particles having a bulk density of at least about 0.45 cc/g, a particle size between about 100 and 200 US mesh, a chromium content of less than 100 ppm;
- and an expansion of about 80 cc/g or greater when heated at about 500° C., said method comprising the sequential steps of:
- sieving natural flake graphite to a nominal size between about 100 and 200 US mesh;
- intercalating the natural flake graphite with acid in the presence of an oxidizing agent;
- washing excess acid with water;
- and neutralizing the intercalated graphite with dilute sodium hydroxide solution.
A method of making expandable graphite particles, said expandable graphite particles having a particle size between about 100 and 200 US mesh, a chromium content of less than 100 ppm;
- and an expansion of about 80 cc/g or greater when heated at about 500° C., said method comprising the sequential steps of:
- sieving natural flake graphite bulk density of at least about 0.48 cc/g, to a nominal size between about 100 and 200 US mesh;
- intercalating the natural flake graphite with acid in the presence of an oxidizing agent;
- washing excess acid with water;
- and
- neutralizing the intercalated graphite with dilute sodium hydroxide solution.