Electroosmotic material, method for production of the material, and electroosmotic flow pump

An electroosmotic material comprising a porous sintered body of a dielectric material, wherein

• when the dielectric material is brought into contact with a liquid, a surface of the dielectric material is electrically charged,
• when a voltage is applied between a first electrode and a second electrode in an electroosmotic flow pump, the electroosmotic material generates an electroosmotic flow in a direction from the first electrode to the second electrode or a reverse direction,
• 0.05 to 10 parts by weight in total of at least one component selected from the group consisting of natural minerals containing an aluminum silicate salt, BaSiO3, BaTiO3, BaZrO3, SrSiO3, and SiC is added to 100 parts by weight of a fused quartz or a fused silicic acid, and
• the fused quartz or the fused silicic acid has an average particle diameter of 0.2 to 7.5 μm.

An electroosmotic material comprising a porous sintered body of a dielectric material, wherein

• when the dielectric material is brought into contact with a liquid, a surface of the dielectric material is electrically charged,
• when a voltage is applied between a first electrode and a second electrode in an electroosmotic flow pump, the electroosmotic material generates an electroosmotic flow in a direction from the first electrode to the second electrode or a reverse direction,
• 0.05 to 10 parts by weight in total of at least one component selected from the group consisting of BaO, SrO, CaO, TiO2, ZrO2, Na2O, and K2O components is added to 100 parts by weight of an SiO2—Al2O3, the mole ratio of a fused quartz or a fused silicic acid:
• a fused alumina being 65 to 99.8:35 to 0.2 in the SiO2—Al2O3, and
• the fused quartz or the fused silicic acid has an average particle diameter of 0.2 to 7.5 μm, and the fused alumina has an average particle diameter of 0.3 to 10 μm.

An electroosmotic material comprising a porous sintered body of a dielectric material, wherein

• when the dielectric material is brought into contact with a liquid, a surface of the dielectric material is electrically charged,
• when a voltage is applied between a first electrode and a second electrode in an electroosmotic flow pump, the electroosmotic material generates an electroosmotic flow in a direction from the first electrode to the second electrode or a reverse direction,
• 0.05 to 10 parts by weight in total of at least one component selected from the group consisting of natural minerals containing an aluminum silicate salt;
• BaSiO3, BaTiO3, BaZrO3, SrSiO3, and SiC is added to 100 parts by weight of an SiO2—Al2O3, the mole ratio of a fused quartz or a fused silicic acid:
• a fused alumina being 65 to 99.8:35 to 0.2 in the SiO2—Al2O3, and
• the fused quartz or the fused silicic acid has an average particle diameter of 0.2 to 7.5 μm, and the fused alumina has an average particle diameter of 0.3 to 10 μm.

A method for producing an electroosmotic material, comprising the steps of:

• adding 0.05 to 10 parts by weight in total of a powder containing at least one component selected from the group consisting of BaO, SrO, CaO, TiO2, ZrO2, Na2O, and K2O components or at least one component selected from the group consisting of natural minerals containing an aluminum silicate salt, BaSiO3, BaTiO3, BaZrO3, SrSiO3, and SiC to 100 parts by weight of a fused quartz powder or a fused silicic acid powder to obtain a mixed powder;
• calcining the mixed powder at 800° C. to 1280° C. to obtain a calcine;
• milling the calcine to obtain a calcined powder having an average particle diameter of 0.1 to 8.5 μm;
• adding a binder to the calcined powder, and forming the resultant mixture to obtain a shape;
• and
• sintering the shape at 1000° C. to 1350° C. to obtain a porous sintered body, wherein
• the fused quartz powder or the fused silicic acid powder has an average particle diameter of 0.2 to 7.5 μm.

A method for producing an electroosmotic material, comprising the steps of:

• adding 0.05 to 10 parts by weight in total of a powder containing at least one component selected from the group consisting of BaO, SrO, CaO, TiO2, ZrO2, Na2O, and K2O components or at least one component selected from the group consisting of natural minerals containing an aluminum silicate salt, BaSiO3, BaTiO3, BaZrO3, SrSiO3, and SiC to 100 parts by weight of an SiO2—Al2O3 powder, the mole ratio of a fused quartz or a fused silicic acid:
• a fused alumina being 65 to 99.8:35 to 0.2 in the SiO2—Al2O3 powder to obtain a mixed powder;
• calcining the mixed powder at 800° C. to 1280° C. to obtain a calcine;
• milling the calcine to obtain a calcined powder having an average particle diameter of 0.1 to 8.5 μm;
• adding a binder to the calcined powder, and forming the resultant mixture to obtain a shape;
• and
• sintering the shape at 1000° C. to 1350° C. to obtain a porous sintered body, wherein
• the fused quartz powder or the fused silicic acid powder has an average particle diameter of 0.2 to 7.5 μm, and the fused alumina powder has an average particle diameter of 0.3 to 10 μm.