Thin Film Semiconductor Device and Method for Manufacturing the Same

Abstract

An Mo film (6) is formed on a SiO2 film (5) by particularly using the film thickness and the deposition temperature (ambient temperature in a sputtering chamber) as the primary parameters and adjusting the film thickness to be within the range from 100 nm to 500 nm (more preferably 100 nm to 300 nm) and the deposition temperature to be within the range from 25° C. to 300° C., so as to control residual stress to have a predetermined value of 300 MPa or greater and to be oriented to increase the in-plane lattice constant. There can be thus provided a reliable CMOSTFT in which desired strain is easily and reliably imparted to polysilicon thin films (4a and 4b) to improve the mobility therein without adding an extra step of imparting the strain to the silicon thin film.