Abstract

This disclosure is aimed at providing a method for producing an epitaxial wafer allowing uniform occurrence of oxygen precipitate in a substrate plane in the radial direction in a base plate and excelling in the crystal quality of an epi-layer. A method for the production of an epitaxial wafer, characterized by using as a substrate a base plate of nitrogen- and carbon-added silicon single crystal having a nitrogen concentration of 5×1014 to 5×1015 atoms/cm3 and a carbon concentration of 1×1016 to 1×1018 atoms/cm3, having a crystal growth condition during the production of silicon single crystal in a range in which the whole surface of substrate becomes an OSF region, and being pulled at a cooling speed of not less than 4° C./minute between 1100 and 1000° C. during the growth of crystal, and depositing the silicon single crystal layer on the surface of the substrate by the epitaxial method.