Thermal spray powder and process for producing the same as well as method for spraying the same
OwnerTsuyoshi Itsukaichi, Satoru Osawa +1inventors
InventorsTsuyoshi Itsukaichi, Satoru Osawa, Isao Aoki
Life of this patent
Estimating the term…
Abstract
A thermal spray powder of the present invention includes particles composed of molybdenum disulfide, and a coating layer provided on the surface of each of the particles. The coating layer is composed of a metal that is softened or melted at a temperature lower than the heat decomposition temperature of the molybdenum disulfide. The coating layer is preferably composed of copper. The thermal spray powder suppresses heat decomposition of the molybdenum disulfide contained in the thermal spray powder during thermal spraying.
Claims11
(canceled)
The method according to claim 10, wherein the coating layer is provided on the entire surface of the each particle.
The method according to claim 10, wherein the content of the molybdenum disulfide in the thermal spray powder is 30% to 90% by weight, and the content of the metal in the thermal spray powder is 10% to 70% by weight.
The method according to claim 10, wherein the metal is copper.
The method according to claim 10, said preparing the thermal spraying powder includes providing the coating layer by an electroless plating method.
(canceled)
A method for forming a thermally sprayed coating containing molybdenum disulfide, the method comprising:
- preparing a thermal spray powder, wherein the thermal spray powder includes:
- particles composed of molybdenum disulfide;
- and
- a coating layer provided on a surface of each of the particles, wherein the coating layer is composed of a metal that is softened or melted at a temperature lower than the heat decomposition temperature of the molybdenum disulfide;
- and
- thermal spraying the thermal spray powder, using a high-velocity flame spraying machine, at a temperature less than the heat decomposition temperature of molybdenum disulfide and not less than the softening or melting temperature of the metal composing the coating layer to form the thermally sprayed coating.
(canceled)
Dependencies are inferred from the claim text.