Oxide layer-containing zirconium-niobium alloy tibial plateau prosthesis having bone trabecula and preparation method

A preparation method of the tibial plateau prosthesis with trabeculae containing zirconium-niobium alloy on oxidation layer comprising the following steps:

• 1) Using zirconium-niobium alloy powder as a raw material, conducting a 3D printing for one-piece molding, and obtaining a first intermediate of the tibial plateau prosthesis with trabeculae containing zirconium-niobium alloy on oxidation layer, putting the first intermediate into a Sinter-hip furnace, heating to 1250° C.-1400° C. under inert gas protection, placing at a constant pressure of 140 MPa-180 MPa for 1 h to 3 h, reducing to a normal pressure, cooling to below 200° C. with the furnace, taking the first intermediate out, and obtaining a second intermediate of the tibial plateau prosthesis with trabeculae;
• 2) Placing the second intermediate product in a programmable thermostat to cool to −80° C. to −120° C. at a rate of 1° C./min, keeping the second intermediate product at a constant temperature for 5 h to 10 h, and taking the second intermediate product out of the programmed thermostat;
• placing the second intermediate product in a liquid nitrogen for 16 h to 36 h, and adjusting the temperature to a room temperature so as to obtain a third intermediate;
• 3) Placing the third intermediate product in a programmable thermostat to cool to −80° C. to −120° C. at a rate of 1° C./min, and placing the third intermediate product at a constant temperature for 5 h to 10 h, taking the third intermediate product out of the programmed thermostat, placing the third intermediate in the liquid nitrogen for 16 h to 36 h and adjusting the temperature to room temperature so as to obtain a fourth intermediate;
• 4) Machining, finishing, polishing, cleaning, and drying the fourth intermediate product, and obtaining a fifth intermediate, where the upper surface roughness of the fifth intermediate tibial plateau support is Ra≤0.050 μm;
• 5) Putting the fifth intermediate product into a tube furnace, introducing a atmospheric pressure inert gas containing 5% to 15% of oxygen in percentage by mass, heating to 500° C. to 700° C. at 5° C./min to 20° C./min, and cooling to 400° C. to 495° C. at 0.4° C./min to 0.9° C./min, and cooling to be below 200° C. sequentially, taking the fifth intermediate product out to obtain the tibial plateau prosthesis with trabeculae containing zirconium-niobium alloy on oxidation layer;
• the structure of the tibial plateau prosthesis with trabeculae containing zirconium-niobium alloy on oxidation layer is the same as its first intermediate product, second intermediate product, third intermediate product, fourth intermediate product, and fifth intermediate product;
• wherein the inert gas is helium or argon;
• the tibial plateau prosthesis with trabeculae containing zirconium-niobium alloy on oxidation layer includes a kidney-shaped plateau support (1), a Y-shaped protrusion (3) is provided on the upper surface of the inwardly curved portion of the kidney-shaped plateau support (1), a rear groove is (5) provided on the lateral surfaces of the two branches of the Y-shaped protrusion (3), a curved protrusion (2) is provided on the upper surface of the outwardly curved portion of the kidney-shaped plateau support (1) corresponding to the Y-shaped protrusion (3);
• a front groove (6) is arranged on the inner side of the curved protrusion (2), the middle part of the lower surface of the kidney-shaped plateau support (1) is provided with a handle (4), and a trabeculae (9) is arranged on the lower surface of the kidney-shaped plateau support (1) excepting connecting the handle (4), the trabeculae (9) is composed of a proximal trabecular layer (21) which is closed to the plateau support (1) and a distal trabecular layer (20) which is away from the plateau support (1);
• the pore size and porosity of the proximal trabecular layer (21) are evenly arranged, and the distal trabecular layer (20) are partitioned into three partitions;
• the transverse diameter (10) of the corresponding kidney-shaped plateau support (1) is divided into a first section (25), a second section (26) and a third section (27) by a first marking point (11) and a second marking point (12);
• and the lengths of the first section, the second section and the third section are 25%-38%, 24%-50% and 25%-38% of the transverse diameter of the kidney-shaped plateau support (1), respectively, a first section line (13) passes through the first marking point (11), a second section line (14) passes through the second marking point (12);
• and the first section line (13) and the second section line (14) are straight lines or arcs, which separate the distal trabecular layer (20) into an inner portion trabeculae (15), an intermediate portion trabeculae (16) and an outer portion trabeculae (17);
• the pore size and porosity of the trabeculae in the inner portion (15) are sequentially larger than those in the outer portion (17) and the intermediate portion (16).